Critical examination of fatigue thresholds

Proceedings of the TMS Fall Meeting

Volumn , Issue , 2002, Pages 259-262

  Sadananda, K ^a   Holtz, R L ^a   Vasudevan, A K ^b  

^a NAVAL RESEARCH LABORATORY   (United States)

^b OFFICE OF NAVAL RESEARCH   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

CRACK PROPAGATION; CRACKS; FRACTURE; FRACTURE MECHANICS; PLASTIC DEFORMATION; PLASTICITY; STRESS INTENSITY FACTORS; SURFACE ROUGHNESS;

COMPRESSIVE FORCES; DISLOCATION GENERATION; DISLOCATION PROCESSES; FATIGUE THRESHOLDS;

FATIGUE OF MATERIALS;

EID: 0036915044     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (24)

1. P.C. Paris and F. Erdogan, "A Critical Analysis of Crack Propagation Laws", J. Basic Engineering, 85 (1963), 528-534.
2. W. Elber, "Fatigue Crack Closure under Cyclic Tension", Engr. Frac. Mech., 2 (1970), 37-45.
3. K. Sadananda and A.K. Vasudevan, "Short Crack Growth and Internal Stresses", Int. J. Fatigue, 19 (1997), S99-S108.
4. N. Louat, K. Sadananda, M. Duesbery, and A.K. Vasudevan, "A Theoretical Evaluation of Crack Closure", Met. Trans. A, 24 (1993), 2225-2232.
5. P.C. Paris, H. Tada, and J.K. Donald, "Service Load Fatigue Damage - A Historical Perspective", Int. J. Fatigue, 21 (1999), S35-S46.
6. J.K. Donald and P.C. Paris, "An Evaluation of DKeff Estimation Procedures on 6061-T6 and 2024-T3 Aluminum Alloys", Int. J. Fatigue, 21 (1999), S47-S58.
7. A.K. Vasudevan, K. Sadananda and N.Louat, "A Review of Crack Closure, Fatigue-Crack Threshold and Related Phenomena, Mat. Sci. Engr. A, 188 (1994), 1-22.
8. A.K. Vasudevan and K.Sadananda, "Application of the Unified Fatigue Damage Approach to Compression-Tension Region", Int. J. Fatigue, 21 (1999), S263-S273.
9. A.K. Vasudevan and K. Sadananda, "Analysis of Fatigue Crack Growth under Compression-Compression Loading", Int. J. Fatigue, 23 (2001), S365-S374.
10. J.C. Radon, "Fatigue Crack Growth in the Threshold Regime", in Fatigue Thresholds J. Bucklund, et al. eds., (EMAS, Warley, UK 1982), 113-132.
11. M. Lang and X. Huang, "The Influence of Compressive Loads on Fatigue Crack Propagation in Metals", Fat. Frac. Eng. Mat. Struc., 21 (1998), 65-83.
12. J. Weertman, "Crack Tip Blunting by Dislocation Pair Creation and Separation", Phil. Mag. A, 43 (1981), 1103-1123.
13. A.T. Yokobori, Jr. and T. Yokobori, "On Micro-and Macro-Mechanics of Fatigue Thresholds", in Fatigue Thresholds J. Bucklund, et al. eds., (EMAS, Warley, UK 1982), 171-190.
14. K. Tanaka and T. Mura, "Fatigue Crack Growth along Planar Slip Bands", Acta Met, 32 (1984), 1731-1740.
15. V. Weiss and D. Lal, "Threshold Condition for Fatigue Crack Propagation", Met. Trans., 5 (1974), 1946-1949.
16. A.K. Vasudevan and K. Sadananda, "Fatigue Crack Growth in Metal Matrix Composites", Script Met. Et Mat. 28 (1993), 837-842.
17. J. R. Rice and R. Thomson, "Ductile versus Brittle Behavior of Crystals", Phil. Mag., 29 (1974), 73-79.
18. K. Sadananda and D.N. Ramaswamy, "Role of Crack Tip Plasticity in Fatigue Crack Growth", Phil. Mag. A, 81 (2001), 1283-1303.
19. I.H. Lin and R. Thomson, "Overview No. 47 - Cleavage, Dislocation Emission and Shielding for Cracks under General Loading", Acta Met. 34 (1986), 187-206.
20. K. Sadananda and P. Shahinian, "Prediction of Threshold Stress Intensity for Fatigue Crack Growth using a Dislocation Model", Int. J. Fatigue, 13 (1977), 585-594.
21. S. Suresh, Fatigue of Materials, (Cambridge University Press, New York, 1982).
22. K. Sadananda, A.K. Vasudevan, R.L. Holtz and E.U. Lee, "Analysis of Overload Effects and Related Phenomena", Int. J. Fatigue, 21 (1999), S233-S245.
23. C. Laird, "The Influence of Metallurgical Structure on the Mechanics of Fatigue Crack Propagation", in Fatigue Crack Propagation, ASTM-STP 415 (1967), 131-168.
24. P. Neumann, "Coarse Slip Model of Fatigue", Acta Met., 17 (1969), 1219-25.