Delamination cracking in thermal barrier coating system

Journal of Engineering for Gas Turbines and Power

Volumn 124, Issue 4, 2002, Pages 922-930

  Zhou, Y C ^a   Hashida, T ^a  

^a TOHOKU UNIVERSITY   (Japan)

Author keywords

[No Author keywords available]

Indexed keywords

CERAMIC COATINGS; COOLING; CRACK INITIATION; DELAMINATION; HEATING; OXIDATION; THERMAL BARRIER COATINGS; THERMAL STRESS;

ENERGY RELEASE;

GAS TURBINES;

CRACKING; DELAMINATION; MATHEMATICAL ANALYSIS; PROTECTION; THERMAL BARRIER COATING;

EID: 0036825924     PISSN: 07424795     EISSN: None     Source Type: Journal    
DOI: 10.1115/1.1477194     Document Type: Article

References (27)

1. Yuri, I., Hisamatsu, T., Watanabe, K., and Etori, Y., 1997, "Structural Design and High Pressure Test of a Ceramic Combustor for 1500°C Class Industrial Gas Turbine." ASME J. Eng. Gas Turbines Power. 119, pp. 506-511.
2. Kokini, K., and Takeuchi, Y. R., 1996, "Surface Thermal Cracking of Thermal Barrier Coatings Owing to Stress Relaxation: Zirconia vs. Mullite." Surf. Coat. Technol., 82, pp. 77-82.
3. Zhu, D. M., and Miller, R. A., 1998, "Investigation of Thermal High Cycle and Low Cycle Fatigue Mechanisms of Thick Thermal Barrier Coatings." Mater. Sci. Eng., A, 245A, pp. 212-223.
4. Jian, C. Y., 1996, "Study on Evaluation Method of Ceramic Coating System for Gas Turbine Rotator Blades." Doctor's thesis. Tohoku University.
5. 3 Scales During the Oxidation of Fe-22Cr-4.8Al-0.3Y Alloy," Acta Mater., 46(3), pp. 927-937.
6. Ogawa, K., Minkov, D., Shoji, T., Sato, M., and Hashimoto, H., 1999, "NDE of Degradation of Thermal Barrier Coating by Means of Impedance Spectroscopy," NDT & E Int., 32, pp. 177-185.
7. Gell, M., et al., 1999, "Mechanism of Spallation in Platinum Aluminide/ Electron Beam Physical Vapor-Deposited Thermal Barrier Coatings," Metall. Trans. A, 30A(2), pp. 427-435.
8. He, M. Y., Evans, A. G., a'nd Hutchinson, J. W., 1998, "Effects of Morphology on the Decohesion of Compressed Thin Films," Mater. Sci. Eng., 245, pp. 168-181.
9. Bernstein, H. L., and Allen, J. M., 1992, "Analysis of Cracked Gas Turbine Blades," ASME J. Eng. Gas Turbines Power, 114, pp. 293-301.
10. Zhou, Y. C., and Hashida, T., 2000, "Coupled Effects of Temperature Gradient and Oxidation on the Thermal Barrier Coating Failure," Life Assessment of Hot Section Gas Turbine Components, R. Townsend, et al., eds., Cambridge University Press, London, UK, pp. 155-1720.
11. Zhou, Y. C., and Hashida, T., 2002, "Thermal Fatigue in Thermal Barrier Coating," JSME Int. J., A45, pp. 57-64.
12. Zhou, Y. C., and Hashida, T., 2001, "Coupled Effects of Temperature Gradient and Oxidation on the Thermal Stress in Thermal Barrier Coating," Int. J. Solids Struct., 38, pp. 4235-4264.
13. Sih, G. C., Paris, P. C., and Irwin, G. R., 1965, "On Cracks in Rectilinearly Anisotropic Bodies," Int. J. Fract. Mech., 1, pp. 189-203.
14. Rice, J. R., and Sih, G. C., 1965, "Plane Problems of Cracks in Dissimilar Media," ASME J. Appl. Mech., 32, pp. 418-423.
15. Dundurs, J., 1969, "Edge-Bonded Dissimilar Ortogonal Elastic Wedges," ASME J. Appl. Mech., 36, pp. 650-652.
16. Erdogan, F., 1965, "Stress Distribution in Bonded Dissilimar Materials With Cracks," ASME J. Appl. Mech., 32, pp. 403-410.
17. Evans, A. G., and Hutchinson, J. W., 1984, "On the Mechanics of Delamination and Spalling in Compressed Films," Int. J. Solids Struct., 20, pp. 455-466.
18. Hutchinson, J. W., and Suo, Z., 1992, "Mixed Mode Cracking in Layered Materials," Adv. Appl. Mech., 29, pp. 63-191.
19. Timoshenko, S. P., and Gere, J. M., 1972, Mechanics of Materials, D. Van Nostrand, New York.
20. Dundurs, J., 1990, "Boundary Conditions at Interfaces," Micromechanics and Inhomogeneous. G. J. Weng, et al., eds., Springer-Verlag, New York, pp. 109-114.
21. Mura, T., 1982, Micromechanics of Defects in Solid, Martinus Nijhoff Publishers, The Hague.
22. Suo, Z., and Hutchinson, J. W., 1990, "Interface Crack Between Two Elastic Layers," Int. J. Fract., 43, pp. 1-18.
23. Whitney, J. M., and McCullough, R. L., 1990, Micromechanical Materials Modeling, Vol. 2, Technomic Lancaster, PA.
24. Lekhnitskii, S. G., 1963, Theory of Elasticity of an Anisotropic Elastic Body, Holden-Day, Oakland, CA.
25. Suo, Z., 1990, "Delamination Specimens for Orthotropic Materials," ASME J. Appl. Mech., 57, pp. 627-634.
26. Hutchinson, J. W., Mear, M. E., and Rice, J. R., 1987, "Crack Paralleling an Interface Between Dissimilar Materials," ASME J. Appl. Mech., 54, pp. 828-832.
27. Zhou, Y. C., Hashida, T., and Jian, C. Y., 2002, "Determination of Interface Fracture Toughness in Thermal Barrier Coating System by Blister Tests," ASME J. Eng. Mater. Tech., 124, in press.