Volumn 117, Issue 3, 2002, Pages 195-205

A shear lip analysis of concave R-curves for an AlMgZn alloy

Author keywords

[No Author keywords available]

Indexed keywords

CRACKS; ELASTICITY; FRACTURE; PLASTICITY; SHEAR STRESS;

EID: 0036820198     PISSN: 03769429     EISSN: None     Source Type: Journal    
DOI: 10.1023/A:1022050618899     Document Type: Article
Times cited : (2)

References (11)
  • 2
    • 0012293223 scopus 로고    scopus 로고
    • A finite element analysis of stable crack growth in an aluminium alloy
    • in press
    • Cheung, S. and Luxmoore, A.R. (2002b). A finite element analysis of stable crack growth in an aluminium alloy. Engineering Fracture Mechanics (in press).
    • (2002) Engineering Fracture Mechanics
    • Cheung, S.1    Luxmoore, A.R.2
  • 3
    • 0012341413 scopus 로고
    • Effect of specimen size and geometry on ductile crack growth resistance in a C-Mn steel
    • Gibson, G.P., Druce, S.G. and Turner, C.E. (1988). Effect of specimen size and geometry on ductile crack growth resistance in a C-Mn steel. International Journal of Fracture 37, 83-100.
    • (1988) International Journal of Fracture , vol.37 , pp. 83-100
    • Gibson, G.P.1    Druce, S.G.2    Turner, C.E.3
  • 5
    • 0003288677 scopus 로고    scopus 로고
    • Two-parameter fracture assessment of through-thickness cracks in an aluminium bridge structure
    • ECF-11, Futuroscope, France
    • Henry, B.S. and Luxmoore, A.R. (1996). Two-parameter fracture assessment of through-thickness cracks in an aluminium bridge structure. Eleventh European Conference on Fracture, ECF-11, Futuroscope, France.
    • (1996) Eleventh European Conference on Fracture
    • Henry, B.S.1    Luxmoore, A.R.2
  • 6
    • 0030258371 scopus 로고    scopus 로고
    • Elastic-plastic fracture mechanics assessment of low constraint aluminium test specimens
    • Henry, B.S., Luxmoore, A.R. and Sumpter, J.D.G. (1996). Elastic-plastic fracture mechanics assessment of low constraint aluminium test specimens. International Journal of Fracture 81, 217-234.
    • (1996) International Journal of Fracture , vol.81 , pp. 217-234
    • Henry, B.S.1    Luxmoore, A.R.2    Sumpter, J.D.G.3
  • 8
    • 0016962005 scopus 로고
    • Determination of valid R-curves for materials with large fracture toughness to yield strength ratios
    • Mai, Y.W., Atkins, A.G. and Caddell, R.M. (1976). Determination of valid R-curves for materials with large fracture toughness to yield strength ratios. International Journal of Fracture 12, 391-407.
    • (1976) International Journal of Fracture , vol.12 , pp. 391-407
    • Mai, Y.W.1    Atkins, A.G.2    Caddell, R.M.3
  • 9
    • 0001131157 scopus 로고    scopus 로고
    • Observations on tearing instability in an aluminium alloy
    • ECF-112
    • Sumpter, J.D.G. (1996). Observations on tearing instability in an aluminium alloy. Mechanisms and Mechanics of Damage and Failure, ECF-11 2, 855-860.
    • (1996) Mechanisms and Mechanics of Damage and Failure , vol.2 , pp. 855-860
    • Sumpter, J.D.G.1
  • 11
    • 0027187138 scopus 로고
    • Energy dissipation rate and crack opening angle analyses of fully plastic ductile tearing. Constraint effects in fracture
    • Turner, C.E. and Braga, L. (1993). Energy dissipation rate and crack opening angle analyses of fully plastic ductile tearing. Constraint effects in fracture. ASTM STP 1171, 158-175.
    • (1993) ASTM STP , vol.1171 , pp. 158-175
    • Turner, C.E.1    Braga, L.2


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.