Fatigue and Fracture of Engineering Materials and Structures

Volumn 25, Issue 8-9, 2002, Pages 837-844

Very high cycle regime fatigue of thin walled tubes made from austenitic stainless steel

(3) Carstensen, J V a Mayer, H b Brondsted P a

a TECHNICAL UNIVERSITY OF DENMARK (Denmark)

b UNIVERSITY OF NATURAL RESOURCES AND LIFE SCIENCES (Austria)

Author keywords

Bending fatigue; Endurance limit; Frequency influence; Ultrasonic fatigue; Very high cycle fatigue

Indexed keywords

ALLOYING; ALUMINUM ALLOYS; AUSTENITE; COLD WORKING; CRACK INITIATION; CRACK PROPAGATION; FATIGUE OF MATERIALS; FATIGUE TESTING; FRACTURE; SCANNING ELECTRON MICROSCOPY; STRAIN RATE; STRESSES;

BENDING FATIGUE; ENDURANCE LIMIT; FREQUENCY INFLUENCE; ULTRASONIC FATIGUE;

STAINLESS STEEL;

EID: 0036672712 PISSN: 8756758X EISSN: None Source Type: Journal
DOI: 10.1046/j.1460-2695.2002.00554.x Document Type: Article

Times cited : (35)

References (30)

1
- 0019144408
- Ultrasonic fatigue
- (1980) Int. Met. Rev. , vol.2 , pp. 65-78
- Willertz, L.E.¹

2
- 0001453069
- Ultrasonic fatigue testing
- (Edited By J. R. Newby, J. R. Davis, S. K. Refsnes and D. A. Dietrich). ASTM, Philadelphia
- (1992) ASM Handbook , vol.8 , pp. 240-258
- Roth, L.D.¹

3
- 0032682530
- Fatigue crack growth and threshold measurements at very high frequencies
- (1999) Int. Mat. Rev. , vol.44 , pp. 1-36
- Mayer, H.¹

4
- 0020305989
- Strain rate sensitivity effects in cyclic deformation and fatigue fracture
- (Edited by J. M. Wells, O. Buck, L. D. Roth and J. K. Tien). The Metallurgical Society of AIME, Philadelphia
- (1982) Ultrasonic Fatigue , pp. 187-205
- Laird, C.P.¹ Charsley, P.²

5
- 0019558540
- Cyclic deformation and fatigue behaviour of aα-iron mono- and poly-crystal
- (1981) Int. J. Fract. , vol.17 , pp. 193-220
- Mughrabi, H.¹ Herz, K.² Stark, X.³

6
- 0028518028
- Influence of cycling frequency on strain localization and cyclic deformation in fatigue
- (1994) Mater. Sci. Engng. , vol.187 , pp. 23-35
- Mayer, H.¹ Laird, C.²

7
- 0037186805
- Cyclic plastic deformation of tantalum and niobium at very high numbers of cycles
- (2002) Mater. Sci. Engng. , vol.A325 , pp. 520-524
- Papakyriacou, M.¹ Mayer, H.² Plenk, H.³ Tschegg, S.⁴

8
- 0035973448
- Influence of loading frequency on high-cycle fatigue properties of b.c.c. and h.c.p. metals
- (2001) Mater. Sci. Engng. , vol.A308 , pp. 143-152
- Papakyriacou, M.¹ Mayer, H.² Pypen H.P., Jr.³ Stanzl-Tschegg, S.⁴

9
- 0020298953
- On the fatigue of copper up to ultrasonic frequencies
- The Metallurgical Society of AIME, Philadelphia
- (1982) Proceedings of the 1st International Conference on Fatigue and Corrosion Fatigue Up to Ultrasonic Frequencies , pp. 265-282
- Roth, L.D.¹ Willertz, L.E.² Leax, T.R.³

10
- 0026955422
- Low-cycle fatigue of niobium and niobium-1 Pct zirconium alloys
- (1992) Metall. Trans. , vol.23 A , pp. 3077-3084
- Meininger, J.M.¹ Gibeling, J.C.²

11
- 0003899880
- Predicting fatigue properties of cast aluminium by characterizing small-crack propagation behavior
- PhD Dissertation, University of Michigan, Ann Arbon, MI
- (2001)
- Caton, M.J.¹

12
- 0035885468
- Influence of loading frequency on the high cycle fatigue properties of AlZnMgCu1.5 aluminium alloy
- (2001) Mater. Sci. Engn. , vol.A314 , pp. 51-57
- Mayer, H.¹ Papakyriacou, M.² Pippan, R.³ Stanzl-Tschegg, S.⁴

13
- 0032592138
- Frequency and stress ratio effects in high cycle fatigue of Ti-6Al-4V
- (1999) Int. J. Fatigue , vol.21 , pp. 679-685
- Morissey, R.J.¹ McDowell, D.L.² Nicholas, T.³

14
- 0027154473
- Determination of fatigue limit between 105 and 109 cycles using an ultrasonic fatigue device
- ASTM STP 1211, (Edited by. M. R. Mitchell and R. W. Landgraf). ASTM, Philadelphia
- (1993) Advances in Fatigue Lifetime Predictive Techniques , pp. 141-152
- Bathias, C.¹ Jingang, N.²

15
- 0033155569
- The frequency effect on the fatigue crack growth rate of 304 stainless steel
- (1999) Nucl. Engng. Des. , vol.191 , pp. 225-230
- Shih, Y.S.¹ Chen, J.-J.²

16
- 0035342393
- The combined effect of frequency and load level on fatigue crack growth in stainless steel 304
- (2001) Int. J. Fatigue , vol.23 , pp. 417-425
- Baik, Y.M.¹ Kim, K.S.²

17
- 0020271427
- The influence of frequency on fatigue crack propagation of some heat resisting alloys using ultrasonic fatigue
- The Metallurgical Society of AIME. Philadelphia
- (1982) Proceedings of the 1st International Conference on Fatigue and Corrosion Fatigue Up to Ultrasonic Frequencies , pp. 461-472
- Hoffelner, W.¹

18
- 0032626481
- The fatigue limit and its eliminations
- (1999) Fatigue Fract. Engng Mater. Struct. , vol.22 , pp. 545-557
- Miller, K.J.¹ O'Donnell, W.J.²

19
- 0001621591
- Internal friction and fatigue in metals at large strain amplitude
- (1956) J. Acoust. Soc. Am. , vol.28 , pp. 1207-1218
- Mason, W.P.¹

20
- 4243762934
- What is stainless steel
- Document from the Sandvik Steel web-site; (DocumentsInternetWeb)/81268C5B9BABA9C0C1256ACA00271CF9
- (2002)

21
- 0005474523
- Mechanisms of fatigue cracking at and near the threshold
- (1990) Proceedings of the Fatigue 90 - 4th International Conference on Fatigue and Fatigue Thresholds, Engineering Materials, Advisory Service, West Midlands , pp. 1333-1343
- Baïlon, J.P.¹ Dickson, J.I.² Shiqiong, L.³ Larouche, D.⁴

22
- 0023983037
- Fatigue life prediction in fexural bending of hollow cross-sectional bars from axial fatigue information
- (1988) J. Testing Evaluation , vol.16 , pp. 146-152
- Muralidharan, U.¹

23
- 0029360192
- Characterization of cyclic plastic bending of austenitic AISI 304 stainless steel
- (1995) Engng. Fract. Mech. , vol.51 , pp. 1049-1058
- Bayoumi, M.R.¹ Latif, A.K.A.E.²

24
- 0032639632
- Stepwise S-N curve and fish-eye failure in gigacycle fatigue
- (1999) Fatigue Fract. Engng Mater. Struct. , vol.22 , pp. 601-607
- Nishijima, S.¹ Kanazawa, K.²

25
- 0032664906
- Factors influencing the mechanism of superlong fatigue failure in steels
- (1999) Fatigue Fract. Engng Mater. Struct. , vol.22 , pp. 581-590
- Murakami, Y.¹ Nomoto, T.² Ueda, T.³

26
- 0033177737
- Gigacycle fatigue of ferrous alloys
- (1999) Fatigue Fract. Engng Mater. Struct. , vol.22 , pp. 667-672
- Wang, Q.Y.¹ Berard, J.Y.² Dubarre, A.³ Baudry, G.⁴ Rathery, S.⁵ Bathias, C.⁶

27
- 0035657940
- S-N curve characteristics and subsurface crack initiation behaviour in ultra-long life fatigue of a high carbon-chromium bearing steel
- (2001) Fatigue Fract. Engng Mater. Struct. , vol.24 , pp. 781-790
- Shinozawa, K.¹ Lu, L.² Ishihara, S.³

28
- 0034428857
- On the mechanism of fatigue failure in the superlong life regime (> 107 cycles). Part I: Influence of hydrogen trapped by inclusions
- (2000) Fatigue Fract. Engng Mater. Struct. , vol.23 , pp. 893-902
- Murakami, Y.¹ Nomotomo, T.² Ueda, T.³ Murakami, Y.⁴

29
- 0002220942
- The area parameter model for small defects and nonmetallic inclusions in fatigue strength: Experimental evidences and applications
- Birmingham, UK. Engineering Materials Advisory Services Ltd., Cradley Heath, Warley, UK
- (1992) Proceedings of the Theoretical Concepts and Numerical Analysis of Fatigue , pp. 51-71
- Murakami, Y.¹ Endo, M.²

30
- 0032664907
- Application of ultrasound for fatigue testing of lightweight alloys
- (1999) Fatigue Fract. Engng. Mater Struct. , vol.22 , pp. 591-599
- Mayer, H.¹ Lipowsky, H.² Papakyriacou, M.³ Rösch, R.⁴ Stitch, A.⁵ Stanzl-Tschegg, S.⁶

* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.