Evaluation of thermal stresses induced in anisotropic material during thermal shock

Journal of Thermal Stresses

Volumn 25, Issue 7, 2002, Pages 647-661

  Ishihara, Sotomi ^a   Goshima, T ^a   Iwawaki, S ^a   Shimizu, M ^a   Kamiya, S ^a  

^a UNIVERSITY OF TOYAMA   (Japan)

Author keywords

Anisotropy; FEM analysis; Linear expansion coefficient; Quench; Thermal shock; Thermal stresses; Young's modulus

Indexed keywords

ANISOTROPY; CERAMIC MATERIALS; CERMETS; COMPUTER SIMULATION; ELASTIC MODULI; FINITE ELEMENT METHOD; HEAT RESISTANCE; SHOCK TESTING;

THERMAL SHOCK;

THERMAL STRESS;

EID: 0036644429     PISSN: 01495739     EISSN: None     Source Type: Journal    
DOI: 10.1080/01495730290074351     Document Type: Article

References (19)

1. Study on thermal shock behavior of cermets and cemented carbides
2. Cyclic thermal shock tests of cermets and cemented carbides
3. Heat transmission on the thermal shock test of ceramics
4. Crack growth in carburized type 304 stainless steel by thermal striping in sodium
5. Nonpropagation of cracks in cracks of carburized materials caused by thermal striping in sodium
6. Evaluation method of thermal shock resistance of epoxy resin based on fracture mechanics
7. Thermal fatigue behavior of alumina ceramics by water quenching method
8. Estimation of thermal shock resistance of ceramics, 2nd report, heat transfer coefficient and thermal stress at quenching in liquid sodium
9. Estimation of thermal shock resistance of ceramics, 4th report, transient boiling curves of low boiling point medium and thermal stress at quenching
10. Observations on the characteristics of a fluidized bed for the thermal shock testing of brittle ceramics
11. Effect of bath and specimen temperature on the thermal stress resistance of brittle ceramics subjected to thermal quenching
12. Proc. 1st dynamic thermal stress and crack growth behavior due to repeated thermal shock in cemented carbides
13. Crack growth behavior due to repeated thermal shock in cemented carbides and cermets
14. Crack propagation behavior of cermets and cemented carbides under repeated thermal shocks by the improved quench test
15. An improved method for the determination of the maximum thermal stress induced during a quench test
16. On fatigue damage and small crack growth behavior of silicon nitride under cyclic thermal shock loading
17. Measurement of transient thermal stresses induced during improved quench-tests
18. Thermal expansion coefficient and thermal conductivity of WC based cemented carbides