Elimination of surface defects in cold-rolled extra low carbon steel sheet

Iron and Steelmaker (I and SM)

Volumn 29, Issue 6, 2002, Pages 23-26

  Genzano, C ^a   Madias, J ^a   Dalmaso, D ^a   Petroni, J ^a   Biurrun, D ^a   Di Gresia, G ^a  

^a NONE

Author keywords

[No Author keywords available]

Indexed keywords

COLD ROLLING; COMPOSITION EFFECTS; CRACK PROPAGATION; DEFECTS; SOLUBILITY; SURFACE PROPERTIES;

DEPTH MEASUREMENT; EXTRA LOW CARBON; SIDERAR SLABS; SURFACE DEFECTS;

CARBON STEEL;

EID: 0036607342     PISSN: 02758687     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (11)

1. Influence of shell solidification on generation of slab defects. Use of hydraulic mold oscillation at Sollac Florange
2. The formation of oscillation marks in the continuous casting of steel slabs
3. Optimization of mold oscillation pattern for the improvement of surface quality and lubrication in slab continuous casting
4. The mechanisms for sticking type breakouts and new developments in continuous casting mold fluxes
5. Mold fluxes in high speed thin slab casting
6. Reduction of pencil pipe defects at LTV Steel's Cleveland Works No. 1 Continuous caster
7. Experiment to simulate superficial too-shallow-to-identify sliver defects on cold-rolled steel
8. Formation of surface heat crack in low carbon steels during hot rolling
9. The prevention of steelmaking source iron oxide defects
10. Controlling the occurrence of sliver defects at Dofasco
11. An AISI-Sponsored collaborative project on FeO-type sliver defects