Volumn 9, Issue 2, 2002, Pages 167-184

Characteristics of hydrogen embrittlement, stress corrosion cracking and tempered martensite embrittlement in high-strength steels

(4) Eliaz, N a,d Shachar, A b,c Tal, B b Eliezer, D c

a MASSACHUSETTS INSTITUTE OF TECHNOLOGY (United States)

b Metallurgical Laboratory (Israel)

c BEN GURION UNIVERSITY OF THE NEGEV (Israel)

d TEL AVIV UNIVERSITY (Israel)

Author keywords

Failure analysis; Hydrogen embrittlement; Stress corrosion cracking; Structural steel; Tempered martensite embrittlement

Indexed keywords

FABRICATION; FRACTOGRAPHY; LANDING GEAR (AIRCRAFT); MARTENSITE; MICROHARDNESS; OPTICAL MICROSCOPY; SCANNING ELECTRON MICROSCOPY; STEEL; STRESS CORROSION CRACKING; X RAY DIFFRACTION ANALYSIS;

HIGH-STRENGTH STEEL;

HYDROGEN EMBRITTLEMENT;

EMBRITTLEMENT; FAILURE ANALYSIS; HIGH STRENGTH STEEL; HYDROGEN EMBRITTLEMENT; MARTENSITE; STRESS CORROSION CRACKING;

EID: 0036532858 PISSN: 13506307 EISSN: None Source Type: Journal
DOI: 10.1016/S1350-6307(01)00009-7 Document Type: Article

Times cited : (241)

References (38)

1
- 0003923309
- New York: Macmillan, (333-55)
- (1992) Principles and Prevention of Corrosion , pp. 234-289
- Jones, D.A.¹

2
- 0028450194
- Failures of structures and components by environmentally assisted cracking
- (1994) Eng Failure Anal , vol.1 , Issue.2 , pp. 77-90
- Lynch, S.P.¹

3
- 0017915575
- Intergranular failure in steel: The role of grain-boundary composition
- (1978) Int Met Rev , vol.23 , Issue.4 , pp. 164-199
- Briant, C.L.¹ Banerji, S.K.²

4
- 0020930453
- Intergranular fracture in ferrous alloys in nonaggressive environments
- Briant C.L., Banerji S.K., editors. New York: Academic Press
- (1983) Treatise on Materials Science and Technology , vol.25 , pp. 21-58
- Briant, C.L.¹ Banerji, S.K.²

5
- 0003687445
- 4th ed. New York: John Wiley and Sons, 485-520
- (1996) Deformation and Fracture Mechanics of Engineering Materials , pp. 460-464
- Hertzberg, R.W.¹

6
- 0020943936
- Hydrogen embrittlement
- Briant C.L., Banerji S.K., editors. New York: Academic Press
- (1983) Treatise on Materials Science and Technology , vol.25 , pp. 275-359
- Nelson, H.G.¹

7
- 0016961794
- Hydrogen transport by dislocations
- (1976) Metall Trans A , vol.7 A , Issue.6 , pp. 821-829
- Tien, J.K.¹ Thompson, A.W.² Bernstein, I.M.³ Richards, R.J.⁴

8
- 84933195593
- A theory of the fracture of metals
- (1957) Adv Phys , vol.6 , Issue.24 , pp. 418-465
- Stroh, A.N.¹

9
- 0015300738
- A new model for hydrogen-assisted cracking (hydrogen "embrittlement")
- (1972) Metall Trans , vol.3 , Issue.2 , pp. 437-451
- Beachem, C.D.¹

10
- 0023827822
- Hydrogen embrittlement of alpha titanium: In situ TEM studies
- (1988) Acta Metall , vol.36 , Issue.1 , pp. 111-124
- Shih, D.S.¹ Robertson, I.M.² Birnbaum, H.K.³

11
- 0002472167
- Mechanisms of hydrogen related fracture of metals
- Moody N.R., Thompson A.W., editors. Wyoming, 1990: Warrendale: TMS
- (1989) Proceedings of the Fourth International Conference on the Effect of Hydrogen on the Behavior of Materials , pp. 639-660
- Birnbaum, H.K.¹

12
- 0030129276
- Hydrogen embrittlement characterization by disk pressure tests: Test analysis and application to high chromium martensitic steels
- (1996) J Eng Mater Technol , vol.118 , Issue.2 , pp. 179-185
- Beghini, M.¹ Benamati, G.² Bertini, L.³

13
- 0030283340
- Compositional variation of hydrogen permeability in ferritic alloys and steels
- (1996) J Nucl Mater , vol.238 , Issue.2-3 , pp. 189-197
- Jung, P.¹

14
- 0030410173
- Effects of Ni, Si and Cu on the properties of steel bars for prestressed concrete
- (1996) NKK Tech Rev , vol.75 , pp. 11-18
- Shiraga, T.¹ Ishiguro, M.² Yamashita, E.³ Mizoguchi, S.⁴

15
- 0027588629
- Roles of microalloying elements in hydrogen induced cracking resistant property of HSLA steels
- (1993) Corrosion , vol.49 , Issue.5 , pp. 389-398
- Liou, H.Y.¹ Shieh, R.I.² Wei, F.I.³ Wang, S.C.⁴

16
- 0024107047
- Effects of Mo, V, Nb, Ti, Zr and their carbides on the corrosion and hydrogen uptake of iron in sulfuric acid
- (1988) Werkst Korros , vol.39 , Issue.11 , pp. 525-533
- Riecke, E.¹ Johnen, B.² Liesegang, H.³ Thoms, A.⁴ Reynders, B.⁵ Grabke, H.J.⁶

17
- 0026398283
- Noble metal implantation to reduce hydrogen embrittlement in steels
- (1991) Surf Coat Technol , vol.49 , Issue.1-3 , pp. 500-503
- Buckley, P.¹ Placzankis, B.² Lowder, L.³ Brown, I.G.⁴ Brown, R.⁵

18
- 0032659523
- Clean steel technology - Fundamental to the development of high performance steels
- Mahaney J.K. Jr., editor. West Conshohocken: ASTM, ASTM STP, 1361
- (1999) Advances in the Production and Use of Steel with Improved Internal Cleanliness , pp. 73-88
- Wilson, A.D.¹

19
- 0016028447
- The intergranular embrittlement of nickel by hydrogen: The effect of grain boundary segregation
- (1974) Metall Trans A , vol.5 , Issue.2 , pp. 483-492
- Latanision, R.M.¹ Opperhauser H., Jr.²

20
- 0016426551
- Further observation on the effect of grain boundary segregation in the hydrogen embrittlement of nickel
- (1975) Metall Trans A , vol.6 , Issue.1 , pp. 233-234
- Latanision, R.M.¹ Opperhauser H., Jr.²

21
- 0022146537
- The chemistry of fracture: A basis for analysis
- (1985) Acta Metall , vol.33 , Issue.10 , pp. 1769-1783
- Eberhart, M.E.¹ Latanision, R.M.² Johnson, K.H.³

22
- 0021444687
- A molecular orbital model of intergranular embrittlement
- (1984) Acta Metall , vol.32 , Issue.6 , pp. 955-959
- Eberhart, M.E.¹ Johnson, K.H.² Latanision, R.M.³

23
- 0022961693
- The electrochemistry and solid state chemistry of intergranular hydrogen embrittlement
- Jones R.H., Gerberich W.W., editors. Toronto, 1986: Warrendale: TMS
- (1985) Proceedings of the Symposium on Modeling Environmental Effects on Crack Growth Processes , pp. 125-136
- Eberhart, M.E.¹ Latanision, R.M.²

24
- 0028449451
- Hydrogen embrittlement of microalloyed structural steels
- (1994) Werkst Korros , vol.45 , Issue.6 , pp. 349-354
- Vehovar, L.¹

25
- 0031632664
- Hydrogen induced cracking processes in structural microalloyed steels: Characterization and modelling
- Rodriguez-Ibabe, Gutiérrez I., López B., editors. Basque Country, 1998. Mater Sci Forum, Switzerland: Trans. Tech. Publ
- (1998) Proceedings of the International Conference on Microalloying in Steels , vol.284-286 , pp. 303-310
- Alvarez Laso, J.A.¹ Gutiérrez-Solana, F.²

26
- 0027224367
- Effect of cold drawing on susceptibility to hydrogen embrittlement of prestressing steel
- (1993) Mater Struct , vol.26 , pp. 30-37
- Toribio, J.¹ Lancha, A.M.²

27
- 17944395198
- Hydrogen inventory and embrittlement in low activation steels
- (1998) J Nucl Mater , vol.258-263 , pp. 124-129
- Jung, P.¹

28
- 0008268833
- Stress-corrosion cracking
- 9th ed. Ohio: ASM International
- (1987) Metals Handbook , vol.13 , pp. 145-163
- Jones, R.H.¹ Ricker, R.E.²

29
- 34249661993
- Stress corrosion cracking
- Gangloff R.P., Ives M.B., editors. Wisconsin. Houston, 1990: NACE
- (1988) Proceedings of the First International Conference on Environment-Induced Cracking of Metals , pp. 1-19
- Parkins, R.N.¹

30
- 2042485576
- editors. Unieux-Firminy, 1973. Houston: NACE
- (1977) Proceedings of the Conference on Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys
- Staehle, R.W.¹ Hochmann, J.² McCright, R.D.³ Slater, J.E.⁴

31
- 2042489694
- AMS 6415. SAE Standard, January
- (1999) Steel Bar Forging and Tubing (0.8Cr 1.8Ni 0.25Mo 0.38-0.43C (SAE 4340))

32
- 0003572836
- P.S. 01.9001. Israel Aircraft Industry
- (1984) Heat Treatment of Carbon and Low Alloy Steels Other Than Case Hardening and Tool Steels

33
- 33847672948
- ASTM F 519. West Conshohocken: ASTM
- (1993) Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating Processes and Service Environments

34
- 0003822491
- QQ-C-320 Federal Specification
- (1987) Chromium Plating (Electrodeposited)

35
- 2042484757
- QQ-P-416. Federal Specification, May
- (1995) Plating, Cadmium (Electrodeposited)

36
- 0003890880
- ASTM E 8. West Conshohocken: ASTM
- (1999) Standard Test Methods for Tension Testing of Metallic Materials

37
- 2042456774
- ASTM G 38. West Conshohocken: ASTM
- (1973) Standard Practice for Making and Using C-ring Stress-corrosion Test Specimens

38
- 60049091411
- ASTM G 44. West Conshohocken: ASTM
- (1994) Standard Practice for Exposure of Metals and Alloys by Alternate Immersion in Neutral 3.5% Sodium Chloride Solution

* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.