Contact fatigue failure analysis of shot-peened gears

Engineering Failure Analysis

Volumn 9, Issue 2, 2002, Pages 147-158

  Guagliano, M ^a   Riva, E ^b   Guidetti, M ^c  

^a POLITECNICO DI MILANO   (Italy)

^b UNIVERSITY OF PARMA   (Italy)

^c Casappa SpA   (Italy)

Author keywords

Carburization; Fatigue crack growth; Gear tooth failures; Residual stress; Shot peening

Indexed keywords

GEARS; MICROCRACKS; RESIDUAL STRESSES; SCANNING ELECTRON MICROSCOPY; SHOT PEENING;

SHOT-PEENED GEARS;

FATIGUE OF MATERIALS;

CARBURIZING; FAILURE ANALYSIS; FATIGUE; GEAR TOOTH; RESIDUAL STRESS; SHOT PEENING;

EID: 0036532836     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/S1350-6307(01)00002-4     Document Type: Article

References (13)

1. The significance of Almen intensity for the generation of shot peening residual stresses
2. Effect of shot peening on contact fatigue behavior life of carburized steel
3. Effect of shot peening on the pitting fatigue strength of carburized gears
4. Effect of shot peening on contact fatigue behavior of 40Cr steel after compound heat treatment
5. Effect of material, heat treatment, grinding and shot peening on contact fatigue life of carburised steels
6. Simulation of the surface fatigue growth under contact loading
7. A fracture mechanics model for the wear of gear flanks by pitting
8. An approach to relate the shot peening parameters to the induced residual stresses
9. Short and long fatigue crack growth - A unified model
10. Materials science perspective of metal fatigue resistance