Three-dimensional numerical investigation of brittle bond fracture

International Journal of Fracture

Volumn 114, Issue 2, 2002, Pages 153-165

  Jensen, Henrik Myhre ^a  

^a TECHNICAL UNIVERSITY OF DENMARK   (Denmark)

Author keywords

Bond fracture; Crack shape; Fracture criteria; Interface fracture; Three dimensional fracture

Indexed keywords

CRACKS; FRACTURE MECHANICS; INTERFACES (MATERIALS); NUMERICAL METHODS;

BOND FRACTURES;

NUMERICAL ANALYSIS;

BRITTLE FRACTURE; CRACK INITIATION; CRACK PROPAGATION; FRACTURE MECHANICS; INTERFACE; WELD;

EID: 0036506935     PISSN: 03769429     EISSN: None     Source Type: Journal    
DOI: 10.1023/A:1015066711279     Document Type: Article

References (11)

1. Mixed mode cracking in layered materials
2. A numerical method for delamination in composites
3. Effects of residual stresses in the blister test
4. Decohesion of a cut prestressed film on a substrate
5. The effect of strength mis-match on mechanical performance of weld joints
6. Fracture mechanics analysis of the fatigue behaviour of spot welds
7. Local fatigue strength characteristics values for spot welded joints
8. Interface comer failure analysis of joint strength: Effect of adherend stiffness
9. Elastic fracture mechanics concepts for interfacial cracks
10. Interface crack between two elastic layers
11. Stress intensities at spot welds