A 3D damage analysis of low-velocity impacts on laminated composites

Composites Science and Technology

Volumn 62, Issue 4, 2002, Pages 585-589

  Guinard, S ^a   Allix, O ^b   Guedra Degeorges D ^a   Vinet, A ^a  

^a AIRBUS GROUP INNOVATIONS   (Germany)

^b Université Paris Saclay   (France)

Author keywords

C. Damage mechanics; C. Delamination; Impact

Indexed keywords

CRACKS; DELAMINATION; LOADING; MATHEMATICAL MODELS; SENSITIVITY ANALYSIS;

DAMAGE MECHANISM; LOW-VELOCITY IMPACTS;

LAMINATED COMPOSITES;

COMPUTER SIMULATION; CRACKING; DELAMINATION; IMPACT; LAMINATE;

EID: 0036500014     PISSN: 02663538     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0266-3538(01)00153-1     Document Type: Article

References (14)

1. Compression strength after impact of a carbon laminate: Failure mechanisms and numerical simulations
2. Delamination in cross-ply laminated composite subjected to low-velocity impact
3. A model for predicting damage in graphite/epoxy laminated composites resulting from low-velocity point impact
4. Estimation of low-velocity impact damage in laminated composite plates using finite element analysis
5. Fracture mechanics and mechanisms of impact-induced delamination in laminated composites
6. Sur la mécanique de l'endommagement des composites
7. Damage analysis of delamination around a hole
8. Modelling of impact damage in composite laminates
9. Damage in composite materials due to low velocity impact
10. Use of statical indentation laws in the impact analysis of laminated composite plates
11. Damage modelling of the elementary ply for laminated composites
12. Sur une famille d'algorithmes en mécanique des structures