Heating during shearing and opening dominated dynamic fracture of polymers

Experimental Mechanics

Volumn 42, Issue 1, 2002, Pages 107-114

  Bjerke, Todd ^a   Lambros, John ^b  

^a UNIVERSITY OF DELAWARE   (United States)

^b UNIVERSITY OF ILLINOIS AT URBANA CHAMPAIGN   (United States)

Author keywords

Dynamic fracture; Impact; Polymers; Shear; Temperature rise; Thermo mechanical coupling

Indexed keywords

CRACK PROPAGATION; FRACTURE MECHANICS; GLASS TRANSITION; INFRARED RADIATION; POLYCARBONATES; REMOTE SENSING; THERMAL EFFECTS;

DYNAMIC FRACTURE;

POLYMETHYL METHACRYLATES;

FRACTURE; HEATING; POLYMER;

EID: 0036494752     PISSN: 00144851     EISSN: None     Source Type: Journal    
DOI: 10.1177/0018512002042001795     Document Type: Article

References (22)

1. Mechanism of fracture in glassy polymers. IV. Temperature rise at the tip of propagating crack in poly(methyl methacrylate)
2. Thermomechanical coupling effects on fractured solids
3. Measurement of the temperature field induced by dynamic crack growth in beta-C titanium
4. The temperature rise at the tip of fast moving cracks in glassy polymers
5. Application of an energy balance and an energy method to dynamic crack propagation
6. Experimental investigation of transient thermoelastic effects in dynamic fracture
7. Failure mode transition at high rates of shear loading
8. Temperature measurements during the formation of shear bands in a structural steel
9. On the failure mode transitions in polycarbonate under dynamic mixed mode loading
10. Failure mode transitions in polymers under high strain rate loading
11. Cracks faster than the shear wave speed
12. Partition of plastic work into stored energy in metals
13. Dynamic thermomechanical behavior of fiber reinforced composites
14. On the extent of dominance of asymptotic elastodynamic crack-tip fields: Pt. 2 - Numerical investigation of three-dimensional and transient effects
15. Dynamically propagating shear bands in impact-loaded prenotched plates - 1. Experimental investigations of temperature signatures and propagation speed
16. Experimental investigation of transient thermoplastic effects in dynamic fracture
17. Fractography and failure mechanisms of amorphous thermoplastics
18. Energy dissipation in dynamic fracture
19. On the dependence of the dynamic crack tip temperature fields in metals upon crack tip velocity and material parameters
20. Investigation of the mechanics of intersonic crack propagation along a bimaterial interface using coherent gradient sensing and photoelasticity