Effects of mode mix upon fracture behavior of a solder joint

International Journal of Fracture

Volumn 113, Issue 3, 2002, Pages 195-212

  Kang, Ki Ju ^a   Kim, Dong Hak ^a   Choi, Seon Ho ^a  

^a Chonnam National University   (South Korea)

Author keywords

Compact tension shear (CTS); Interface crack

Indexed keywords

BOUNDARY LAYERS; CRACK PROPAGATION; FINITE ELEMENT METHOD; FRACTOGRAPHY; FRACTURE MECHANICS; FRACTURE TOUGHNESS; NUCLEATION; STRAIN; STRESS ANALYSIS;

COMPACT-TENSION-SHEAR (CTS) SPECIMEN;

SOLDERED JOINTS;

COMPOSITE; CUTTING TOOL; DUCTILITY; FIBER-REINFORCED MATERIAL; FRACTURE MECHANICS; SHEAR STRESS;

EID: 0036466245     PISSN: 03769429     EISSN: None     Source Type: Journal    
DOI: 10.1023/A:1014264930542     Document Type: Article

References (20)

1. Elastic-plastic fracture behavior of an aluminum alloy under mixed mode loading
2. Fracture of a ductile layer constrained by stiff substrates
3. The fracture resistance of metal-ceramic interfaces
4. II and J-integral for CTS specimen under mixed mode loading
5. Mixed mode cracking in layered materials
6. Plastic zone size near the crack tip in a constrained ductile layer under mixed mode loading
7. Stress distribution near an interface crack tip in a ductile adhesive layer
8. Fracture behavior of 63Sn-37Pb solder
9. Fracture and fatigue crack growth along aluminum-alumina interface
10. Fracture toughness of alumina-niobium interfaces: Experiments and analyses
11. On the ductile enlargement of voids in triaxial stress fields
12. A loading device for the criterion of mixed mode in fracture mechanics
13. Experimental determination of silica/copper interfacial toughness
14. On the toughness of ductile adhesive joints
15. Ductile failure of a constrained metal foil
16. A continuum damage model for ductile fracture of weld heat affected zone