Thin layer splitting along the elastic-plastic solid surface

International Journal of Fracture

Volumn 113, Issue 3, 2002, Pages 233-252

  Wei, Yueguang ^a  

^a INSTITUTE OF MECHANICS   (China)

Author keywords

Elastic plastic solids; Fracture toughness; Peel test; Residual curvature; Split test; Steady state condition

Indexed keywords

BENDING (DEFORMATION); CRACKS; ENERGY DISSIPATION; FRACTURE TOUGHNESS; PLASTICS; STRENGTH OF MATERIALS;

SOLID SURFACE;

FRACTURE;

FRACTURE TOUGHNESS;

EID: 0036466237     PISSN: 03769429     EISSN: None     Source Type: Journal    
DOI: 10.1023/A:1014230227262     Document Type: Article

References (22)

1. On non-local flow theories that preserved the classical structure of incremental boundary value problems
2. On the role of gradients in the localization of deformation and fracture
3. Quasi-static steady crack growth in small scale yielding
4. Interface adhesion: Effects of plasticity and segregation
5. Strain gradient plasticity
6. Mechanism-based strain gradient plasticity - II. Theory
7. Mechanical effects of peel adhesion test
8. Elasto-plastic analysis of the peel test
9. Elasto-plastic analysis of the peel test for thin film adhesion
10. The peeling of flexible laminates
11. Analysis of the peel test: Prediction of adherend plastic dissipation and extraction of fracture energy in metal-to-metal adhesive joints
12. A continuum model for void nucleation by inclusion debonding
13. A theory for cleavage cracking in the presence of plastic flow
14. Determining the toughness of plastically deforming joints
15. Toughness of plastically-deforming asymmetric joints
16. The relation between crack growth resistance and fracture process parameters in elastic-plastic solids
17. The influence of plasticity on mixed mode interface toughness
18. Nonlinear delamination mechanics for thin films
19. Steady-state crack growth and work of fracture for solids characterized by strain gradient plasticity
20. Interface strength, work of adhesion and plasticity in the peel test
21. Models of interface separation accompanied by plastic dissipation at multiple scales
22. Numerical simulations of adhesively-bonded beams failing with extensive plastic deformation