Influence of casting defects on the endurance limit of aluminium and magnesium cast alloys;Einfluss von gussfehlern auf die dauerfestigkeit von aluminium- und magnesiumgusslegierungen

Materialwissenschaft und Werkstofftechnik

Volumn 33, Issue 3, 2002, Pages 117-127

  Mayer, H ^a   Fuchs, U ^b   Tschegg, S ^b   Zettl, B ^b   Lipowsky, Hj ^c   Stich, A ^c   Papakyriacou, M ^d  

^a UNIVERSITY OF NATURAL RESOURCES AND LIFE SCIENCES   (Austria)

^b Institut für Meteorologie und Physik   (Austria)

^c AUDI AG   (Germany)

^d AUSTRIAN INSTITUTE OF TECHNOLOGY   (Austria)

Author keywords

[No Author keywords available]

Indexed keywords

ALUMINUM CASTINGS; CRACKS; DIE CASTING; DURABILITY; FATIGUE OF MATERIALS; FATIGUE TESTING; FRACTURE; HIGH PRESSURE EFFECTS IN SOLIDS; MAGNESIUM CASTINGS; METAL CASTING; POROSITY; PROBABILITY; SHRINKAGE; STRESS INTENSITY FACTORS; ULTRASONIC EQUIPMENT;

CAST ALLOYS; CASTING DEFECTS;

ALUMINUM ALLOYS;

EID: 0036346766     PISSN: 09335137     EISSN: None     Source Type: Journal    
DOI: 10.1002/1521-4052(200203)33:3<117::AID-MAWE117>3.0.CO;2-7     Document Type: Article

References (19)

1. Casting defects and the fatigue behavior of an aluminium casting alloy
2. In-service loading of AlSi11 cast aluminum alloy in the very high cycle regime
3. Modeling the long-life fatigue behavior of a cast aluminium alloy
4. Fatigue life assessment of aluminium alloys with casting defects
5. The effect of solidification rate on the growth of small fatigue cracks in a cast 319-type aluminium alloy
6. Analysis of stress intensity factors of modes I, II and III for inclined surface cracks of arbitrary shape
7. Effects of defects, inclusions and inhomogeneities on fatigue strength
8. Application of ultrasound for fatigue testing of lightweight alloys
9. Microstructural effects on high-cycle fatigue-crack initiation in a 356.2 casting alloy
10. Korrosionsermüdung verschiedener aluminium- und magnesium-gusslegierungen
11. Fatigue properties of high pressure die cast magnesium alloys at high numbers of cycles
12. Mechanical properties of magnesium low-pressure permanent mould casting AZ91 under various conditions
13. Mechanical properties of magnesium die casting alloys at elevated temperatures and microstructure in dependence of wall thickness
14. Fatigue crack growth and threshold measurements at very high frequencies
15. Propagation and non-propagation of short fatigue cracks at a sharp notch
16. th of small cracks emanating from small defects
17. The effective threshold of fatigue crack propagation in aluminium alloys, Part I: Influence of yield stress and chemical composition
18. Fatigue of AZ91E-T6 cast magnesium alloy