Degradation of aluminum metal matrix composites in salt water and its control

Materials and Design

Volumn 23, Issue 2, 2002, Pages 173-180

  Ahmad, Zaki ^a   Abdul Aleem, B J ^a  

^a KING FAHD UNIVERSITY OF PETROLEUM AND MINERALS   (Saudi Arabia)

Author keywords

Composites; Corrosion; Inhibitors

Indexed keywords

ALUMINUM ALLOYS; CORROSION RESISTANCE; DEGRADATION; POLYSTYRENES; PROTECTIVE COATINGS; SODIUM CHLORIDE; SOLUTIONS;

DISLOCATION DENSITY;

METALLIC MATRIX COMPOSITES;

ALUMINUM; COMPOSITE; CORROSION CONTROL; CORROSION INHIBITOR; SALINE WATER; SILICON CARBIDE;

ALLOY; ALUMINUM; CORROSION CONTROL; INHIBITOR; SALT WATER;

PERSIAN GULF;

EID: 0036207774     PISSN: 02641275     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (22)

1. Aluminum alloys in desalination service
2. An electrochemical evaluation of 3003, 3004 and 5050 aluminum alloys for desalination plants
3. An electrochemical evaluation of 1100, 5052 and 6063 aluminum alloys for desalination
4. Corrosion of aluminum alloys
5. Intergranular corrosion of an aluminum-magnesium-silicon-copper alloy
6. The processing and properties of discontinuously reinforced aluminum composite
7. Corrosion behaviour of SiC/Al metal matrix composite
8. Mechanism of aqueous corrosion of aluminum at 100°C
9. The influence of corrosion and hydrogen cracking on blast wear in wet media
10. Electrochemical measurements in flowing solutions
11. The potential of freshly generated metal surface determined from the guillotined electrode. A new technique
12. On the synergistic effect of abrasion and corrosion during wear
13. The effect of abrasive particle size on the slurry erosion resistance of particulae-reinforced aluminum alloy
14. Corrosion behavior of silicon carbide particle-reinforced 6061/Al alloy composites
15. Effect of temper on seawater corrosion of an aluminum-silicon carbide composite alloy
16. Inhibition of flow-induced corrosion of Al 6013-20SiC(P)-T4 composite in 3.5 wt.% neutral sodium chloride solution
17. Effect of velocity and elevated temperature on pitting of Al 6013-20SK(P) composite in 3.5 wt.% NaCl