Fatigue of drillstring: State of the art;Fatigue des tiges de forage: État de l'art

Oil and Gas Science and Technology

Volumn 57, Issue 1, 2002, Pages 7-37

  Vaisberg, O ^a   Vincke O ^a   Perrin, G ^a   Sarda, J P ^a   Fay J B ^a  

^a IFP ENERGIES NOUVELLES   (France)

Author keywords

Corrosion; Damage calculation; Drillpipe; Drillstem; Drillstring; Environmental effects; Failure; Fatigue; Fatigue tests; Improvement; Inspection; Threaded connections; Tool joints

Indexed keywords

CORROSION; DRILL PIPE; FAILURE (MECHANICAL); FATIGUE OF MATERIALS; FATIGUE TESTING; FRACTURE MECHANICS; TORQUE;

FATIGUE DURATIONS;

OIL WELL DRILLS;

DAMAGE ASSESSMENT; DRILL STRING; FATIGUE ANALYSIS; FRACTURE MECHANICS;

EID: 0036118859     PISSN: 12944475     EISSN: None     Source Type: Journal    
DOI: 10.2516/ogst:2002002     Document Type: Article

References (92)

1. New study shows how to predict accumulated drillpipe fatigue
2. An experimental investigation of fatigue-crack growth in drillstring tubulars
3. Ten ways to reduce drilling costs
4. A unified approach to drillstem failure prevention
5. Trip inspection, testing gain favor as insurance
6. La pratique des essais de fatigue
7. Maximum permissible doglegs in rotary boreholes
8. Cumulative fatigue damage of drillpipe in doglegs
9. Recommended practice for drillstem design and operating limits
10. Model predicts drillpipe fatigue in horizontal wells. Maurer engineering Inc
11. Extended drillpipe life with tighter specifications. Gobal marine drilling Co
12. Drill-pipe bending and fatigue in rotary drilling of horizontal wells Maurer engineering Inc
13. Bending stress magnification in constant curvature doglegs with impact on drillstring and casing
14. Systematic tracking of fatigue and crack growth to optimize drillstring reliability. Enertech engineering and research Co
15. Drillpipe for horizontal drilling
16. Designing and qualifying drillstrings for extended reach drilling
17. Drillpipe buckling in inclined holes
18. Helical buckling and lock-up conditions for coiled tubing in curved wells
19. Downhole tool serviceability under dynamic loads
20. Stress concentration incorporated fatigue analysis of die-marked drillpipe
21. Fatigue testing of drillpipe
22. Stress analysis of drillstring threaded connections using the finite element method
23. Fatigue limits analyzed for drillpipe in a dogleg
24. The effect of tool-joint stiffness on drillpipe fatigue in riser ball joints
25. A comparison of fracture mechanics and S-N curve approaches in designing drillpipe
26. Drillpipe fatigue life prediction model based on critical plane approaches
27. Drillstring fatigue performance
28. A comparison of fracture mechanics and S-N curve approaches in designing drillpipe
29. Fracture mechanics concept offers model to help calculate fatigue life in drillpipe
30. Qualifying drillstring components for deep drilling
31. Successful reduction of North sea drillstring failures
32. Case history of drillstem failures offshore West Africa
33. New technology for the inspection of used tubing and drillpipe
34. Recommended practice for field inspection of new casing, tubing and plain end drillpipe
35. Drillstring problems related to internal upset-run-cut area of drillpipe. Tuboscope Inc
36. Sensitivity and application of the normal beam ultrasonic technique for detection of fatigue cracks in rotary shouldered connections
37. Ultrasonics finds frillpipe cracks
38. Recent advances in used drillpipe inspection by ultrasonic methods
39. Determining drillpipe wear inside casing using ultrasonic measurements
40. Inspection interval guidelines to reduce drillstring failures
41. Drillpipe inspection technique
42. Reliability methods applied to drilling operations
43. An integrated approach to enhancing the mechanical life of drillpipe in extended reach wells
44. Field correlation between internal taper length and tube failures in 4.5-in. 16.60E, IEU drillpipe
45. Corrosion fatigue of AISI 4145 steel in drilling mud
46. Drillstring failure database: What do we learn? API/IADC
47. Fatigue of drillstring connections
48. Near-threshold fatigue crack propagation behavior of a low alloy steel in pressurized dilute brine solution
49. Fatigue of drillpipe
50. Downhole tool full-scale fatigue test: Experience and practice recommendations
51. Methods for the improvement of drill collar joints evaluated by full-size fatigue tests
52. Reduction in fatigue failures through crack detection by alternating current field measurement
53. 2 and chlorides affect drillpipe fatigue
54. Increasing the fatigue life of 40-Cr steel in drilling muds with corrosion inhibitors
55. Corrosion fatigue in nitrocarburized quenched and tempered steels
56. Drillpipe failures in hydrogen sulfide
57. A new drillpipe design virtually eliminates failures that result from slip damage
58. How to reduce drillstring fatigue failures in a corrosive environment
59. Standard procedure for field testing water-based drilling fluids
60. Standard procedure for field testing oil-based drilling fluids
61. Appropriate design of drillpipe internal uset geometry focusing on fatigue property
62. Making drillpipe upsets which increase fatigue life
63. What difference does internal taper length make on drillpipe fatigue life?
64. A new tool-joint design increases the fatigue life of drillpipe tubes
65. Improvement of drill collar fatigue property by last engaged thread height reduction of pin
66. A means of increasing drill collar connection life. Transactions of the ASME
67. Fatigue life improvement of drill collars through control of bore eccentricity
68. Failure prevention by selection and analysis of drillstem connections
69. Deep drilling practices in mississippi
70. One piece, forged, heavy wall drillpipe: Built stronger for tougher drilling
71. Optimization of rotary-shouldered connection reliability and failure analysis
72. Downhole tools fatigue resistance for different materials
73. Calculating limits for torsion and tensile loads on drillpipe
74. Drillstring design options for extended reach drilling operations
75. Recommended practice for testing of thread compound for rotary shouldered connections
76. Tentative API bulletin on rotary shouldered connection thread compounds
77. Make-up torque and rotary shouldered connection reliability
78. Eliminating twist-offs as a cause of drillstring failure. OCTG special report
79. Technique to assess directly make-up contact stress inside tubular connections
80. Development of lightweight steel drillpipe with 165-ksi yield strength
81. Aluminum drillpipe for directional
82. Tool-joint heat checking while predrilling for auger TLP project
83. Fracture toughness criteria for high-strength drillpipe. Shell Canada Ltd
84. IFP field tests its new trafor MWD system
85. Standard surface measurements sampled at high acquisition rate help in detecting drill string vibrations