Effect of holding at high temperature on delamination strength of 8mass%Y2O3 · ZrO2/CoNiCrAlY thermal barrier coating

Zairyo/Journal of the Society of Materials Science, Japan

Volumn 51, Issue 1, 2002, Pages 101-106

  Gao, Lin ^a   Kato, Masahiko ^a   Nakasa, Keijiro ^a   Bansho, Teruhito ^a   Nishida, Hidetaka ^a  

^a HIROSHIMA UNIVERSITY   (Japan)

Author keywords

Delamination energy; Interfacial damage; Interfacial fracture toughness; Oxide layer thickness; Thermal barrier coating (TBC)

Indexed keywords

ACTIVATION ENERGY; ALUMINA; COBALT ALLOYS; DELAMINATION; FRACTURE TOUGHNESS; INTERFACES (MATERIALS); PLASMA SPRAYING; SUPERALLOYS; TENSILE TESTING; ZIRCONIA;

BOND COAT; EDGE INDENT TESTS; HIGH VELOCITY OXYGEN FUEL SPRAYING; INTERFACIAL DAMAGE; OXIDE LAYER THICKNESS; TOP COAT;

THERMAL BARRIER COATINGS;