Nucleation and propagation of an edge crack in a uniformly cooled epoxy/glass bimaterial

International Journal of Solids and Structures

Volumn 39, Issue 2, 2001, Pages 325-340

  Reedy Jr, E D ^a   Guess, T R ^a  

^a SANDIA NATIONAL LABORATORIES   (United States)

Author keywords

Corner; Cracking; Edge; Epoxy; Fracture; Glass; Interface; Stress intensity factor; Stress singularity

Indexed keywords

COOLING; CRACK PROPAGATION; GLASS; JOINTS (STRUCTURAL COMPONENTS); LOADING; NUCLEATION; THERMAL EFFECTS; TOUGHNESS;

CRACK NUCLEATION;

CRACKS;

CRACK PROPAGATION; EPOXY RESIN; GLASS; STRESS INTENSITY FACTOR;

EID: 0035966311     PISSN: 00207683     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0020-7683(01)00203-7     Document Type: Article

References (29)

1. Edge-bonded dissimilar orthogonal elastic wedges under normal and shear loading
2. On the problem of edge-bonded elastic quarter-planes loaded at the boundary
3. Two edge-bonded elastic wedges of different materials and wedge angles under surface traction
4. Logarithmic singular stress field in a semi-infinite plate consisting of two edge-bonded wedges subjected to surface tractions
5. Singular stress field near the corner of jointed dissimilar materials
6. Residual stress induced fracture in glass-sapphire composites: Planar geometry
7. Power-logarithmic stress singularities at bi-material corners and interface cracks
8. On the decohesion of residually stressed thin films
9. Discussion of edge-bonded dissimilar orthogonal elastic wedges under normal and shear loading
10. A fracture criterion for edge-bonded bimaterial bodies
11. Stress singularities and fracture at interface corners in bonded joints
12. A stress singularity parameter approach for evaluating the interfacial reliability of plastic encapsulated LSI devices
13. Stress singularities in a two-material wedge
14. The decohesion of thin films from brittle substrates
15. Fracture initiation at three-dimensional bimaterial interface corners
16. Prediction of fracture energy and flaw size in lasses from measurements of mirror size
17. Stress singularities at the interface in bonded dissimilar materials under mechanical and thermal loading
18. Stresses near the edge of bonded dissimilar materials described by two stress intensity factors
19. Intensity of the stress singularity at the interface corner between a bonded elastic and rigid layer
20. Asymptotic interface corner solutions for butt tensile joints
21. Connection between interface corner and interfacial fracture analyses of an adhesively bonded butt joint
22. Comparison of butt tensile strength data with interface corner stress intensity factor prediction
23. Interface corner stress states: Plasticity effects
24. Interface corner failure analysis of joint strength: Effect of adherend stiffness
25. Additional interface corner toughness data for an adhesively-bonded butt joint
26. Steady-state cracking in brittle substrates beneath adherent films
27. The edge cracking and spalling of brittle plates
28. The stress intensity factor in bonded quarter planes after a change in temperature
29. Stress singularities resulting from various boundary conditions in angular corners of plates in extension