Development of the T0 reference temperature from precracked Charpy specimens

Engineering Fracture Mechanics

Volumn 68, Issue 7, 2001, Pages 861-894

  Joyce, James A ^a   Tregoning, Robert L ^b  

^a UNITED STATES NAVAL ACADEMY   (United States)

^b NAVAL SURFACE WARFARE CENTER   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

BRITTLENESS; CONSTRAINT THEORY; CRACK PROPAGATION; DUCTILITY; FAILURE ANALYSIS; FRACTURE TOUGHNESS; PHASE TRANSITIONS; PROBABILITY DISTRIBUTIONS;

FERRITIC STEELS;

STEEL;

FRACTURE MECHANICS; STEEL;

EID: 0035957759     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0013-7944(00)00135-1     Document Type: Article

References (19)

1. o, for ferritic steels in the transition range
2. o, for ferritic steels in the transition region
3. Numerical investigation of 3-D constraint effects on brittle fracture in SE (B) and C (T) specimens
4. Empirical validation of the master curve for irradiated and unirradiated reactor pressure vessel steels
5. On the utilization of high rate Charpy test results and the master curve to obtain accurate lower bound toughness predictions in the ductile-to-brittle transition
6. Application of the master curve method to crack initiation and crack arrest
7. Effect of constraint on specimen dimensions needed to obtain structurally relevant toughness measures
8. Master curve analysis of ductile to brittle transition region, fracture toughness round robin data: The "Euro" fracture toughness curve
9. Development of a methodology for the assessment of shallow-flaw fracture in nuclear reactor pressure vessels: Generation of biaxial shallow-flaw fracture toughness data
10. c for a 3-D flaw geometry
11. Assessment of the ductile-to-brittle transition toughness behaviour of an A508 class 3 PWR pressure vessel steel by a statistical approach
12. Fracture toughness measurements in the transition regime using small size samples
13. Ductile-to-brittle transition characterization using surface crack specimens loaded in combined tension and bending
14. Application of master curve technology to biaxial and shallow crack fracture data for A533B steels
15. J and CTOD estimation equations for shallow cracks in single edge notch bend specimens
16. Validity of small specimen fracture toughness estimates neglecting constraint corrections
17. Dislocation-mechanics-based constitutive relations for material dynamics calculations
18. Specimen size requirements for fracture toughness testing in the transition region
19. A Weibull stress model to predict cleavage fracture in plates containing surface cracks