Fatigue and durability of silane-bonded epoxy/glass interfaces

Journal of Adhesion

Volumn 76, Issue 4, 2001, Pages 335-351

  Ritter, J E ^a   Learned, J C ^a   Jacome, G S ^a   Russell, T P ^a   Lardner, T J ^a  

^a University of Massachusetts   (United States)

Author keywords

Durability; Epoxy glass interfaces; Fatigue crack growth; Polymer adhesion; Silane bonding

Indexed keywords

AGING OF MATERIALS; BONDING; COMPRESSION TESTING; CRACK INITIATION; CRACK PROPAGATION; CYCLIC LOADS; DURABILITY; FATIGUE OF MATERIALS; GLASS; INTERFACES (MATERIALS); SILANES; THERMAL EFFECTS; X RAY PHOTOELECTRON SPECTROSCOPY;

STATIC LOADS;

EPOXY RESINS;

EID: 0035761410     PISSN: 00218464     EISSN: None     Source Type: Journal    
DOI: 10.1080/00218460108030725     Document Type: Article

References (15)

1. Kinloch, A.J., Adhesion and Adhesives: Science and Technology (Chapman and Hall, London, 1987).
2. Plueddemann, E.P., Silane Coupling Agents, 2nd edn. (Plenum Press, New York, 1991).
3. Ritter, J.E., Fox, J.R., Hutko, D.I. and Lardner, T.J., "Moisture-assisted Crack Growth at Epoxy-Glass Interfaces", J. Mater. Sci. 33, 4581-88 (1998).
4. Turner, M.R., Dalgleish, B.J., Yitte, M. and Evans, A.G., "A Fracture Resistance Measurement Method for Biomaterial Interfaces Having Large Debond Energy", Acta Metall. Mater. 43, 3459-65 (1995).
5. He, M.Y., Turner, M.R. and Evans, A.G., "Analysis of the Double Cleavage Drilled Compression Specimen for Interface Fracture Energy Measurements Over a Range of Mode Mixities", Acta Metall. Mater. 43, 3453-58 (1995).
6. Suo, Z. and Hutchinson, J.W., "Sandwich Test Specimens for Measuring Interface Crack Toughness", Mater. Sci. and Engin. A107, 135-43 (1989).
7. Wang, D. and Jones, F.R., "Surface Analytical Study of the Interaction Between γ-amino-Propyltriethoxysilane and E-Glass Surface, Part II, X-ray Photoelectron Spectroscopy", J. Mater. Sci. 28, 2481-88 (1993).
8. Pawson, D. and Jones, F.R., "The Effect of Sodium Ions on the Stability of the Interphase Region of Glass Fiber Reinforced Composites", J. Adhesion 52, 187-207 (1995).
9. Lawn, B.R., Fracture of Brittle Solids, 2nd edn., Cambridge Univ. Press, Cambridge, 1993.
10. Evans, A.G. and Fuller, E.R., "Crack Propagation in Ceramic Materials Under Cyclic Bond Conditions", Met. Trans. 5, 27-33 (1974).
11. Liechti, K.M. and Chai, S., "Asymmetric Shielding in Interracial Fracture Under Inplane Shear", ASME J. Appl. Mech. 59, 295-304 (1992).
12. Swadener, J.G., Liechti, J.G. and De Lozanne, A.L., "The Intrinsic Toughness and Adhesion Mechanisms of a Glass/Epoxy Interface", J. Mech. and Phys. Solids 47, 223-58 (1999).
13. Ritter, J.E., Sioui, D.R. and Lardner, T.J., "Indentation Behavior of Polymer Coatings on Glass", Polym. Eng. and Sci. 32, 1366-71 (1992).
14. Wool, R.P., Polymer Interfaces, Hanser/Gardner Pub., Cincinnati, 1995.
15. Ritter, J.E., Conley, K.M., Gu, W. and Lardner, T.J., "Observations on FingerLike Crack Growth at a Urethane Acrylate/Glass Interface", J. Adhesion 39, 173-84 (1992).