Crack Growth along Interfaces in Porous Ceramic Layers

Journal of the American Ceramic Society

Volumn 84, Issue 9, 2001, Pages 2051-2059

  Sørensen, Bent F ^a   Horsewell, Andy ^a  

^a TECHNICAL UNIVERSITY OF DENMARK   (Denmark)

Author keywords

[No Author keywords available]

Indexed keywords

BENDING MOMENTS; CRACK PROPAGATION; FRACTURE; INTERFACES (MATERIALS); LANTHANUM COMPOUNDS; POROUS MATERIALS; SCANNING ELECTRON MICROSCOPY;

FRACTURE ENERGY; LANTHANUM STRONTIUM CHROMITE; LANTHANUM STRONTIUM MANGANITE; POROUS CERAMIC LAYERS; SCANNING ELECTRON MICROSCOPE;

CERAMIC MATERIALS;

EID: 0035470658     PISSN: 00027820     EISSN: None     Source Type: Journal    
DOI: 10.1111/j.1151-2916.2001.tb00957.x     Document Type: Article

References (31)

1. K. Kendall, "Transition between Cohesive and Interfacial Failure in a Laminate," Proc. R. Soc. London, A344, 287-302 (1975).
2. M. D. Thouless, H. C. Cao, and P. A. Mataga, "Delamination from Surface Cracks in Composite Materials," J. Mater. Sci. 24, 1406-12 (1989).
3. M.-Y. He and J. W. Hutchinson, "Crack Deflection at an Interface between Dissimilar Elastic Materials," Int. J. Solids Struct., 25, 1053-6767 (1989).
4. W. J. Clegg, "The Fabrication and Failure of Laminar Ceramic Composites," Acta Metall. Mater., 40, 3085-93 (1992).
5. W. J. Clegg, K. Kendall, N. McN, Alford, T. W. Button, and J. D. Birchall, "A Simple Way to Make Tough Ceramics," Nature (London), 347, 455-57 (1990).
6. M. C. Shaw, D. B. Marshall, M. S. Dadkhah, and A. G. Evans, "Cracking and Damage Mechanisms in Ceramic/Metal Multilayers," Acta Metall. Mater., 41, 3311-22 (1993).
7. Q. Ma, M. C. Shaw, M.-Y. He, B. J. Dalgleish, D. R. Clarke, and A. G. Evans, "Stress Redistribution in Ceramic/Metal Multilayers Containing Cracks," Acta Metall. Mater., 43, 2137-42 (1995).
8. H. Liu and S. M. Hsu, "Fracture Behavior of Multilayer Silicon Nitride/Boron Nitride Ceramics," J. Am. Ceram. Soc., 79, 2452-57 (1996).
9. P. E. D. Morgan and D. B. Marshall, "Ceramic Composites of Monazite and Alumina," J. Am. Ceram. Soc., 78, 1552-63 (1995).
10. K. M. Liechti and Y.-S. Chai, "Biaxial Loading Experiments for Determining Interfacial Fracture Toughness," J. Appl. Mech., 58, 680-87 (1991).
11. A. G. Evans and J. W. Hutchinson, "Effect of Nonplanarity on the Mixed Mode Fracture Resistance of Bimaterial Interfaces," Acta Metall., 37, 909-16 (1989).
12. V. Tvergaard and J. W. Hutchinson, "The Influence of Plasticity on Mixed Mode Interface Toughness," J. Mech. Phys. Solids, 41, 1119-35 (1993).
13. L. J. Gibson and M. F. Ashby, Cellular Solids. Pergamon Press, New York, 1998.
14. K. S. Blanks, A. Kristoffersen, E. Carlström, and W. J. Clegg, "Crack Deflection in Ceramic Laminates Using Porous Interlayers," J. Eur. Ceram. Soc. 18, 1945-51 (1998).
15. R. W. Rice, "The Porosity Dependence of Physical Properties of Materials: A Summary Review," Key Eng. Mater., 115, 1-20 (1996).
16. D. D. D. Lam, F. Lange, and A. G. Evans, "Mechanical Properties of Partially Dense Alumina Produced from Powder Compacts," J. Am. Ceram. Soc., 77, 2113-17 (1994).
17. A. R. Boccaccini, "Influence of Stress Concentrations on the Mechanical Property-Porosity Correlation in Porous Materials," J. Mater. Sci. Lett., 17, 1273-75 (1998).
18. J. Dundurs, "Discussion on 'Edge-Bonded Dissimilar Orthogonal Elastic Wedges under Normal and Shear Loading'," J. Appl. Mech., 36, 650-52 (1969).
19. M. L. Williams, "The Stresses around a Fault or Crack in Dissimilar Media," Bull. Seismol. Soc. Am., 49, 199-204 (1959).
20. J. R. Rice, "Elastic Fracture Mechanics Concepts for Interfacial Cracks," J. Appl. Mech., 55, 98-103 (1988).
21. Z. Suo and J. W. Hutchinson, "On Sandwich Test Specimen for Measuring Interface Crack Toughness," Mater. Sci. Eng., A107, 135-42 (1989).
22. S. W. Freiman, D. R. Mulville, and P. W. Mast, "Crack Propagation Studies in Brittle Materials," J. Mater. Sci., 8, 1527-33 (1973).
23. H. Toftegaard, unpublished research.
24. P. V. Hendriksen, private communication.
25. B. Kindl, private communication.
26. B. F. Sørensen, A. Horsewell, O. Jørgensen, A. N. Kumar, and P. Engbærk, "A Fracture Resistance Measurement Method for In Situ Observation of Crack Mechanisms in Brittle Materials," J. Am. Ceram. Soc., 81, 661-69 (1998).
27. S. Ho and Z. Suo, "Tunnelling Cracks in Constrained Layers," J. Appl. Mech., 60, 890-94 (1993).
28. M.-Y. He and J. W. Hutchinson, "Kinking of a Crack out of an Interface," J. Appl. Mech., 56, 270-78 (1989).
29. M.-Y. He, A. Bartlett, A. G. Evans, and J. W. Hutchinson, "Kinking of a Crack out of an Interface: Role of In-Plane Stress," J. Am. Ceram. Soc., 74, 767-71 (1991).
30. S.-X. Gong and H. Horii, "General Solution to the Problem of Microcracks near the Tip of a Main Crack," J. Mech. Phys. Solids, 37, 27-46 (1989).
31. B. F. Sørensen, S. Sarraute, O. Jørgensen, and A. Horsewell, "Thermally Induced Delamination of Multilayers," Acta Mater., 46, 2603-15 (1998).