Influence of threshold parameters on cleavage fracture predictions using the Weibull stress model

International Journal of Fracture

Volumn 110, Issue 3, 2001, Pages 281-304

  Ruggieri, C ^a  

^a UNIVERSITY OF SÃO PAULO   (Brazil)

Author keywords

Cleavage fracture; Constraint; Local approach; Threshold parameter; Weibull stress

Indexed keywords

CALIBRATION; PARAMETER ESTIMATION; STEEL; TOUGHNESS;

WEIBULL STRESS MODELS;

FRACTURE MECHANICS;

CLEAVAGE; FRACTURE; MODELING; STRESS; WEIBULL THEORY;

EID: 0035425313     PISSN: 03769429     EISSN: None     Source Type: Journal    
DOI: 10.1023/A:1010801603304     Document Type: Article

References (29)

1. Prediction of cleavage fracture events in the brittle-ductile transition region of a ferritic steel
2. A local criterion for cleavage fracture of a nuclear pressure vessel steel
3. A Weibull stress model to predict cleavage fracture in plates containing surface cracks
4. Calibration of Weibull stress parameters using fracture toughness data
5. Generalization of selective integration procedures to anisotropic and nonlinear media
6. Ductile-to-brittle transition characterization using surface crack specimens loaded in combined tension and bending
7. WARP3D: Dynamic nonlinear analysis of solids using a preconditioned conjugate gradient software architecture
8. Estimation procedure for the Weibull oarameters used in the local approach
9. A general treatment of crack tip contour integrals
10. A local approach to cleavage fracture
11. Probabilistic treatment of brittle fracture using two failure models
12. A transferability model for brittle fracture including constraint and ductile tearing effects: A probabilistic approach
13. Probabilistic modeling of brittle fracture including 3-D effects on constraint loss and ductile tearing
14. Constraints effects on reference temperature, TO, for ferritic steels in the transition region
15. Transferability of elastic-plastic fracture toughness using the Weibull stress approach: Significance of parameter calibration
16. Effects of crack depth on elastic plastic fracture toughness
17. The scatter in KIc results
18. Fracture toughness transition curve shape for ferritic structural steels
19. Irradiation damage effects on the fracture toughness transition curve shape for reactor pressure vessel steels
20. Statistical model for carbide induced brittle fracture in steel
21. The phenomenon of rupture in solids
22. The effect of temperature and specimen geometry on the parameters of the local approach to cleavage fracture
23. On the stress distribution at the base of a stationary crack
24. Ductile crack growth. III. Transition to cleavage fracture incorporating statistics