Interface cracks in layered materials subjected to a uniform temperature change

International Journal of Fracture

Volumn 110, Issue 4, 2001, Pages 325-349

  Gaudette, F G ^a   Giannakopoulos, A E ^b   Suresh, S ^b  

^a GE GLOBAL RESEARCH   (United States)

^b Massachusetts Institute of Technology Cambridge   (United States)

Author keywords

Elastoplastic analysis and contact; Interface cracks; Layered structures

Indexed keywords

ALUMINUM COMPOUNDS; SOLUTIONS; THERMAL EFFECTS;

LAYERED MATERIALS;

CRACKS;

CRACKING; FRACTURE MECHANICS; INTERFACE; LAYERED MEDIUM; TEMPERATURE EFFECT;

EID: 0035423693     PISSN: 03769429     EISSN: None     Source Type: Journal    
DOI: 10.1023/A:1010872200886     Document Type: Article

References (20)

1. Fracture mechanics
2. Two edge bonded elastic wedges of different materials and wedge angles under surface tractions
3. Residual stress-driven delamination in deposited multilayers
4. Residual stresses and cracking in brittle solids bonded with a thin ductile layer
5. Effects of interfacial damage on the global and local static response of cross-ply laminates
6. 3 interfaces
7. The strength and fracture of metal/ceramic bonds
8. Kinking of a crack out of an interface
9. Laminate delamination due to thermal gradients
10. Thermal stress at the edge of a bimetallic thermostat
11. A criterion for plane strain, fully plastic, quasi-steady crack growth
12. Three-dimensional stress fields of elastic interface cracks
13. Family of crack-tip fields characterized by a triaxiality paramter: Part I - Structure of fields
14. Elasto-plastic analysis of layered materials under thermal loading: Edge Cracks parallel to the interface
15. Elasto-plastic deformation of multi-layered materials during thermal cycling
16. Prediction of arbitrary crack growth from the interface between two dissimilar elastic materials
17. Interface crack between two elastic layers
18. Elasto-plastic analysis of thermal cycling: Layered materials with sharp interfaces