Prediction of the strength of notched fiber-dominated composite laminates

Composites Science and Technology

Volumn 61, Issue 9, 2001, Pages 1311-1321

  Chen, Puhui ^a   Shen, Zhen ^a   Wang, Jun Yang ^a  

^a AIRCRAFT STRENGTH RESEARCH INSTITUTE OF CHINA   (China)

Author keywords

B. Strength; C. failure criterion; Characteristic length; Fiber dominated laminates; Notch

Indexed keywords

FAILURE ANALYSIS; NUMERICAL ANALYSIS; STRENGTH OF MATERIALS;

NOTCHED FIBER-DOMINATED COMPOSITE LAMINATES;

LAMINATED COMPOSITES;

FIBER REINFORCED COMPOSITE; LAMINATE; STRENGTH; TENSILE PROPERTY;

EID: 0035396413     PISSN: 02663538     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0266-3538(01)00030-6     Document Type: Article

References (36)

1. Stress fracture criteria for laminated composites containing concentrations
2. Uniaxial failure of composite laminates containing concentrations
3. Effective stress fracture models for unnotched and notched multidirectional laminates
4. Macroscopic fracture mechanics of advanced composite materials
5. Fracture mechanics correlation for tensile failure of filamentary composites with holes
6. Tensile fracture of laminates with holes
7. Strength of tensile loaded graphite/ epoxy laminates containing cracks, open and filled holes
8. An effective crack growth model for residual strength evaluation of composite laminates with circular holes
9. Effective crack growth and residual strength of composite laminates with a sharp notch
10. Residual strength of an ARALL laminate containing a crack
11. Post-failure behavior of laminates: II-stress concentration
12. Progressive fracture of fiber composites
13. Progressive damage model for laminated composites containing stress concentration
14. Damage tolerance of laminated composites containing an open hole and subjected to compressive loading. Part I-analysis
15. A progressive failure model for composite laminates containing openings
16. Progressive failure of laminated composite with a hole under compressive loading
17. Notched strength of composite laminates: Predictions and experiments - a review
18. Design and analysis of composite structures with stress concentrations
19. A unifying strain criterion for fracture of fibrous composite laminates
20. Response of notched graphite/expoxy and graphite/PEEK systems
21. Fracture mechanics of notched composite laminates
22. Effect of laminate thickness and specimen configuration on the fracture of laminated composites
23. Damage mechanics of composite materials: II-a damage-based notched strength model
24. Damage mechanics of composite materials: IV-the effect of lay-up on damage growth and notched strength
25. The extension of crack tip damage zones in fiber reinforced composite laminates
26. Fracture criterion for notched thin composite laminates
27. Effect of ply thickness on fracture of notched composite laminates
28. Micromechanics of compression failure in open hole composite laminates
29. A detailed investigation of the micromechanisms of compressive failure in open hole composite laminates
30. A comparison of experimental observations and numerical predictions for the initiation of fiber microbuckling in notched composite laminates
31. The effect of ply thickness on longitudinal splitting and delamination in graphite/epoxy under compressive cyclic load
32. Strength of tensile loaded graphite/epoxy laminates containing cracks, open and filled cracks
33. Design guideline of damage tolerance and durability for composite aircraft structures