Selection of interfacial layer of laminated silicon carbide matrix composites

Kuei Suan Jen Hsueh Pao/ Journal of the Chinese Ceramic Society

Volumn 29, Issue 3, 2001, Pages 226-231

  Yuan, Guangjiang ^a   Luo, Yongming ^a   Chen, Daming ^a   Zhou, Yang ^a   Ouyang, Jun ^a   Pan, Wei ^a  

^a BEIJING INSTITUTE OF AERONAUTICAL MATERIALS   (China)

Author keywords

Boron nitride; Carbon silicate; Interfacial layer; Laminated composites; Metal

Indexed keywords

BENDING STRENGTH; CASTING; GELS; SELECTION; SILICON CARBIDE; TOUGHNESS;

CRACK BLUNTNESS; CRACK DEFLECTION; CRACK PARALLEL PROPAGATION; INTERFACIAL LAYER; SILICON CARBIDE MATRIX LAYER;

LAMINATED COMPOSITES;

EID: 0035381709     PISSN: 04545648     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (15)

1. A simple way to make tough ceramics
2. Design and preparation of silicon nitride composite with high fracture toughness and nacre structure
3. Fracture behavior of multilayer silicon nitride/boron nitride ceramics
4. The role of metal plasticity and interfacial strength in the cracking of metal/ceramic laminates
5. 3
6. Constrained densification of alumina/zirconia hybrid laminates, I experimental observations of processing defects
7. Constrained densification of alumina/zirconia hybrid laminates, II Viscoelastic stress computation
8. Reaction-bonded three-layer alumina-based composites with improved damage resistance
9. Porous interfaces as crack deflecting interlayers in silicon carbide laminates
10. Mechanical performance of multilayered silicon nitride
11. Control strength and toughness of ceramic/metal laminates using interface design