Further analysis of the DCDC specimen with an offset hole

International Journal of Fracture

Volumn 109, Issue 2, 2001, Pages 227-237

  Lardner, T J ^a,b   Chakravarthy, S ^a,b   Quinn, J D ^a,b   Ritter, J E ^a,b  

^a Department of Mechanical and Industrial Engineering ^*  (United States)

^b UNIVERSITY OF MASSACHUSETTS   (United States)

Author keywords

Cracks; DCDC specimen; Fracture; Fracture energy; Fracture specimens; Interfacial energy

Indexed keywords

ADHESIVES;

OFFSET HOLES;

CRACKS;

CLEAVAGE; COMPRESSION; CRACK; DRILLING; FRACTURE MECHANICS;

EID: 0035332075     PISSN: 03769429     EISSN: None     Source Type: Journal    
DOI: 10.1023/a:1011073402984     Document Type: Article

References (6)

1. Analysis of the double cleavage drilled compression specimen for interface fracture energy measurements
2. Mixed mode cracking in layered materials
3. Moisture-assisted crack growth at epoxy-glass interfaces
4. Energy release rate along a three-dimensional crack front in a thermally stressed body
5. Sandwich specimens for measuring interface crack toughness