Volumn 38, Issue 4, 2001, Pages 175-188
|
|
Examination of tarnish films formed during SCC of α-brass in ammoniacal solutions;Untersuchung der während spannungsrisskorrosionsprüfungen an α-messing in ammoniakhaltigen lösungen gebildeten anlaufschichen
a
|
|
Author keywords
[No Author keywords available]
|
|
Indexed keywords
AMMONIUM COMPOUNDS;
ANNEALING;
COLOR;
COPPER;
ENERGY DISPERSIVE SPECTROSCOPY;
FILMS;
OXIDATION;
PH EFFECTS;
SCANNING ELECTRON MICROSCOPY;
STRESS CORROSION CRACKING;
STRUCTURE (COMPOSITION);
THERMAL EFFECTS;
BRASS;
COPPER CORROSION;
CRACKS;
PH;
ALPHA BRASS;
AMMONIACAL SOLUTIONS;
COPPER CONCENTRATION;
FRACTURE SURFACES;
TARNISH FILMS;
BRASS;
STRESS CORROSION CRACKING;
ALPHA BRASS;
AMMONIACAL SOLUTION;
COPPER CONCENTRATION;
FAILURE TIME;
FILM FORMATIONS;
FRACTURE SURFACES;
SAMPLE SURFACE;
SOLUTION PH;
|
|
EID: 0035310015
PISSN: 0032678X
EISSN: None
Source Type: Journal
DOI: None Document Type: Article |
|
Times cited : (4)
|
|
References (25)
|