Biaxial fatigue behaviour of a multidirectional filament-wound glass-fiber/epoxy pipe

Composites Science and Technology

Volumn 61, Issue 4, 2001, Pages 491-502

  Ellyin, F ^a   Martens, M ^a  

^a UNIVERSITY OF ALBERTA   (Canada)

Author keywords

Biaxial cyclic; Fatigue testing; Filament wound; GRP; Leakage failure; Multidirectioanl lay up; Pipe

Indexed keywords

CYCLIC LOADS; FATIGUE TESTING; FILAMENT WINDING; LEAKAGE (FLUID); PIPE; STIFFNESS;

BIAXIAL FATIGUE; DAMAGE INITIATION;

GLASS FIBER REINFORCED PLASTICS;

FATIGUE; FIBER REINFORCED COMPOSITE; GLASS FIBER; TESTING;

EID: 0035272301     PISSN: 02663538     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0266-3538(00)00215-3     Document Type: Article

References (20)

1. Biaxial monotonic behaviour of a multi-directional glass fiber epoxy pipe
2. Predicting the long-term fatigue behaviour of filament wound glass-fiber/epoxy matrix pipes
3. The effect of frequency on the fatigue performance of filament-wound pipes under biaxial loading: Experimental results and damage model
4. Preliminary design of tubular composite strucres using netting theory and composite degradation factors
5. The fatigue behaviour of filament-wound fiberglass/epoxy tubes under cyclic pressure
6. Long-term leakage failure and life prediction of fiber composite laminate tubing under combined internal pressure and axial loading: Theory and experiments
7. Standard practice for obtaining hydrostatic or pressure design basis for "fiberglass" (glass-fiber-reinforced thermosetting resin) pipe and fittings
8. An effective stress parameter for long-term fatigue strength of fiber-reinforced plastic pipes
9. Nova pipeline
10. Effects of anisotropy and inhomogeneity on GRP pressure pipe
11. Personal communination, 2 November 1998
12. Resin selection criteria for "tough" composite structures
13. Fatigue damage evaluation through stiffness measurements in boron-epoxy laminates
14. Fatigue of composite - Fatigue modulus concept and life prediction
15. Fatigue of composite materials-damage model and life prediction
16. Prediction of fatigue life for matrix-dominated composite laminates
17. Long-term fatigue behaviour of composite materials
18. Transverse cracking and stiffness reduction in composite laminates