Off-axis fatigue behaviour and its damage mechanics modelling for unidirectional fibre-metal hybrid composite: GLARE 2

Composites Part A: Applied Science and Manufacturing

Volumn 32, Issue 1, 2001, Pages 13-23

  Kawai, M ^a   Hachinohe, A ^a   Takumida, K ^a   Kawase, Y ^a  

^a UNIVERSITY OF TSUKUBA   (Japan)

Author keywords

[No Author keywords available]

Indexed keywords

APPROXIMATION THEORY; FAILURE ANALYSIS; FATIGUE OF MATERIALS; FATIGUE TESTING; GLASS FIBER REINFORCED PLASTICS; MATHEMATICAL MODELS; STRESS ANALYSIS; TENSILE STRENGTH; TENSILE TESTING;

MACROSCOPIC FATIGUE DAMAGE MECHANICS MODEL; UNIDIRECTIONAL FIBER-METAL LAMINATES;

LAMINATED COMPOSITES;

EID: 0035192758     PISSN: 1359835X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S1359-835X(00)00135-4     Document Type: Article

References (32)

1. Young J.B., Landry J.G.N., Cavoulacos V.N. Crack growth and residual strength characteristics of two grades of glass-reinforced aluminum GLARE. Composite Struct. 27:1994;457-469.
2. Asundi A., Choi A.Y.N. Fiber metal laminates: an advanced material for future aircraft. J Mater Processing Technol. 63:1997;384-394.
3. Marissen R. Flight simulation behavior of aramid reinforced aluminum laminates (ARALL). Engng Fracture Mech. 19:1984;261-277.
4. Hidde J.S., Herakovich C.T. Inelastic response of hybrid composite laminates. J Composite Mater. 26:1992;2-19.
5. Ritchie R.O., Yu W., Bucci R.J. Fatigue crack propagation in ARALL laminates: measurement of the effect of crack-tip shielding from crack bridging. Engng Fracture Mech. 32:1989;361-377.
6. Macheret J., Teply J.L., Winter E.F.M. Delamination shape effects in aramidepoxy-aluminum (ARALL) laminates with fatigue cracks. Polymer Composites. 10-5:1989;322-327.
7. Davidson D.L., Austin L.K. Fatigue crack growth through ARALL-4 at ambient temperature. Fatigue Fracture Engng Mech. 14-10:1991;939-951.
8. Chen J.L., Sun C.T. Modeling of orthotropic elastic-plastic properties of ARALL laminates. Composite Sci Technol. 36:1989;321-337.
9. Staley J.T., Liu J., Hunt W.H. Jr. Aluminum alloys for aerostructures. Adv Mater Processes. 152-4:1997;17-20.
10. Kawai M., Morishita M., Tomura S., Satoh K. Inelastic behavior and strength of fiber-metal hybrid composite: glare. Int J Mech Sci. 40-2/3:1998;183-198.
11. Tsai S.W., Wu E.M. A general theory of strength for anisotropic materials. J Composite Mater. 5:1971;58-80.
12. Owen M.J., Griffith J.R. Evaluation of biaxial stress failure surfaces for a glass fabric reinforced polyester resin under static and fatigue loading. J Mater Sci. 13:1978;1521-1537.
13. Hull D. Introduction to composite materials. 1982;Cambridge University Press, Cambridge.
14. Kachanov L.M. Introduction to continuum damage mechanics. 1986;Martinus Nijhoff, Dordrecht.
15. Lemaitre J. A course on damage mechanics. 2nd ed:1996;Springer, Berlin.
16. Sims DF, Brogdon VH. Fatigue behavior of composites under different loading modes. In: Reifsnider KL, Lauraitis KN, editors. Fatigue of filamentary composite materials. ASTM STP 636, ASTM, 1977. p. 185-205.
17. Hashin Z., Rotem A. A fatigue failure criterion for fiber-reinforced materials. J Composite Mater. 7:1973;448-464.
18. JIS K 7083, Testing method for constant-load amplitude tension-tension fatigue of carbon fibre reinforced plastics. Japanese Industrial Standard, Japanese Industrial Association, 1993.
19. ASTM D3479. Standard test methods for tension-tension fatigue of oriented fiber, resin matrix composites. ASTM Standards and Literature References for Composite Materials, ASTM, 1987. p. 67-70.
20. Schwarmann L. Material data of high-strength aluminium alloys for durability evaluation of structures. 1988;Aluminium, Dusseldorf. (p. 32).
21. Kawai M, Yajima S, Hachinohe A, Takano Y. In preparation.
22. Hahn HT. Fatigue behavior and life prediction of composite laminates. In: Tsai SW, editors. Composite materials: testing and design (Fifth Conference), ASTM STP 674, ASTM, 1979. p. 383-417.
23. Awerbuch J, Hahn HT. Off-axis fatigue of graphite/epoxy composite. Fatigue of fibrous composite materials, ASTM STP 723, ASTM, 1981, p. 243-273.
24. Jessen S.M., Plumtree A. Continuum damage mechanics applied to cyclic behaviour of a glass fibre composite pultrusion. Composites. 22:1991;181-190.
25. Poursartip A., Ashby M.F., Beaumont P.W.R. The fatigue damage mechanics of a carbon fiber composite laminate: I - development of the model. Composite Sci Technol. 25:1986;193-218.
26. Poursartip A., Beaumont P.W.R. The fatigue damage mechanics of a carbon fiber composite laminate: II - life prediction. Composite Sci Technol. 25:1986;283-299.
27. Chrzanowski M. Fatigue of composites: a CDM perspective. Hult J., Rammerstorfer F.G. Engineering mechanics of fibre reinforced polymers and composite structures. 1994;189-208 Springer, Berlin.
28. Tsai G.S., Doyle J.F., Sun C.T. Frequency effects on the fatigue life and damage of graphite/epoxy composites. J Composite Mater. 21:1987;2-13.
29. He QC, Sidoroff F. Modelling of the anisotropic damage of unidirectional composite materials under static and fatigue loading. Proc ICCM7, 1989. p. 454-9.
30. Chaboche J.L., Lesne P.M. A non-linear continuous fatigue damage model. Fatigue Fracture Engng Mater Struct. 11:1988;1-17.
31. Ha S.K., Springer G.S. Time dependent behavior of laminated composites at elevated temperatures. J Composite Mater. 23:1989;1159-1197.
32. Hashin Z. Failure criteria for unidirectional fiber composites. ASME J Appl Mech. 47:1980;329-334.