Failure of cadmium plated maraging steel tension bolt

Engineering Failure Analysis

Volumn 8, Issue 3, 2001, Pages 263-269

  Reddy, K Gangadhara ^a   Jha, Abhay K ^a   Diwakar, V ^a  

^a INDIAN SPACE RESEARCH ORGANISATION   (India)

Author keywords

Electrodeposition; Embrittlement; Hydrogen embrittlement; Threaded fasteners

Indexed keywords

CADMIUM; CORROSION RESISTANCE; ELECTROPLATING; FAILURE ANALYSIS; FASTENERS; INTERFACES (MATERIALS); LUBRICATION; MARAGING STEEL; NONDESTRUCTIVE EXAMINATION; TENSILE STRESS;

TENSION BOLTS; ULTIMATE TENSILE STRESS (UTS);

BOLTS;

BOLT; CADMIUM; FAILURE ANALYSIS; HYDROGEN EMBRITTLEMENT; STEEL; THREADED JOINT;

EID: 0035050484     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/S1350-6307(00)00011-X     Document Type: Article

References (12)

1. A study of hydrogen embrittlement of various alloy
2. Environment sensitive fracture of metals and alloys
3. Hydrogen embrittlement prevention and control
4. The effect of composition and tensile strength on the susceptibility of alloy steels to cadmium plating (hydrogen) embrittlement
5. 18 percent nickel maraging steels