Long-life fatigue design of GRP 500 nodular cast iron components

VTT Tiedotteita - Valtion Teknillinen Tutkimuskeskus

Volumn , Issue 2043, 2000, Pages 3-70

  Marquis, Gary ^a   Solin, Jussi ^a  

^a VTT TECHNICAL RESEARCH CENTRE OF FINLAND   (Finland)

Author keywords

Cast iron; Design; Durability; Fatigue life; Fatigue strength at N cycles; GRP 500; Mechanical properties; Nodular cast iron; Service life

Indexed keywords

EID: 0034580828     PISSN: 12350605     EISSN: 14550865     Source Type: Book Series    
DOI: None     Document Type: Article

References (12)

1. Beretta, S., Blarasin, A., Endo, M., Giunti, T. & Murakami, Y. 1997. Defect tolerant design of automotive components. Int. J. Fatigue, Vol. 19, No. 4, p. 319-333. (Pubitemid 127387715)
2. Marquis, G. 1995. High cycle spectrum fatigue of welded components. Espoo: Technical Research Centre of Finland, VTT Publications 240. 83 p. + app. 100 p.
3. Marquis, G., Rabb, R. & Siivonen, L. 1999. Endurance Limit Design of Spheroidal Graphite Cast Iron Components Based on Natural Defects. In: Fatigue Crack Growth Thresholds, Endurance Limits, and Design, ASTM STP 1372, Newman, J. C. & Piascik, R. S., Eds. West Conshohocken, PA: American Society for Testing and Materials. 14 p.
4. Marquis, G. & Socie, D. 1999. Long Life Torsion Fatigue with Normal Mean Stresses. Fatigue and Fracture of Engineering Materials and Structures. (Accepted for publication.)
5. Murakami, Y. 1996. Effects of small defects and inhomogeneities on fatigue strength: Experiments, model and applications to industry. In: Mechanisms and mechanics of damage and failure - ECF 11, Petit, J., de Fouquet, J., Henaff, G., Villechaise, P. & Dragon, A., Eds. Poitiers-Futuroscope, France, 3-6.9.1996. Pp. 31-42.
6. Rabb, B. R. 1999a. Determination of the Scatter in the Fatigue Limit. Prepared for TKK Graduate seminar KON-67.204 Statistical Aspects of Fatigue and Fracture, Wärtsilä NSD, Vaasa. 13 p.
7. Rabb, B. R. 1999b. Fatigue Testing and its Statistical Evaluation into Design Rules. Tampere, Tampere University of Technology Publications 253. 144 p.
8. Rabb, R. 1999c. Nodular cast iron grade 500-7/ISO 1083 under variable amplitude loading. Wärtsilä NSD Corp., R&C/A2/STRA FA, 21.01.99. 16 p. (Preliminary report.)
9. Rabb, R. 1999d. Simulation of staircase tests. Wärtsilä NSD Corp., R&C/A2/STRA FA, 16.02.99. 40 p.
10. Socie, D.F. & Marquis, G.B. 1999. Multiaxial Fatigue. Warrendale, PA: Society of Automotive Engineers. 502 p.
11. Taivalaho, L. 1999. Effect of casting defects on the fatigue strength of nodular cast iron. Espoo, Helsinki University of Technology. MSc thesis. 84 p.
12. Wallin, K. 1999. The probability of success using deterministic reliability. In: Fatigue Design and Reliability: ESIS Publication 23, Marquis, G. & Solin, J., Eds. Amsterdam: Elsevier Science. Pp. 39-50.