Layered alumina composite tested at high temperature in air

Journal of the American Ceramic Society

Volumn 83, Issue 12, 2000, Pages 3033-3040

  O'Brien, Michael J ^a,b   Capaldi, Franco M ^a   Sheldon, Brian W ^a  

^a Brown University   (United States)

^b AEROSPACE CORPORATION   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ALUMINA; CRACKS; DELAMINATION; DEPOSITION; FRACTURE TOUGHNESS; HIGH TEMPERATURE OPERATIONS; HOT PRESSING; MECHANICAL TESTING; OXIDATION RESISTANCE; PHASE INTERFACES; PHASE TRANSITIONS; THERMAL EFFECTS;

AEROSOL SPRAY DEPOSITION; ALUMINA COMPOSITE; COMPOSITE TOUGHENING; FOUR POINT BENDING; OXIDATION RESISTANT INTERPHASE;

COMPOSITE MATERIALS;

EID: 0034506109     PISSN: 00027820     EISSN: None     Source Type: Journal    
DOI: 10.1111/j.1151-2916.2000.tb01679.x     Document Type: Article

References (28)

1. A. J. Phillipps, W. J. Clegg, and T. W. Clyne, "Fracture Behavior of Ceramic Laminates in Bending - II. Comparison of Model Predictions with Experimental Data," Acta Metall. Mater. 41 [3] 819-27 (1993).
2. H. Liu and S. M. Hsu, "Fracture Behavior of Multilayer Silicon Nitride/Boron Nitride Ceramics," J. Am. Ceram. Soc., 79 [9] 2452-57 (1996).
3. D. Kuo and W. M. Kriven, "A Strong and Damage-Tolerant Oxide Laminate," J. Am. Ceram. Soc., 80 [9] 2421-24 (1997).
4. M. J. O'Brien and B. W. Sheldon, "Porous Alumina Coating with Tailored Fracture Resistance for Alumina Composites," J. Am. Ceram. Soc., 82 [12] 3567-74 (1999).
5. R. Raj, "Fundamental Research in Structural Ceramics for Service Near 2000°C," J. Am. Ceram. Soc., 82 [12] 3567-74 (1993).
6. K. K. Chawla, Cermic Matrix Composites, p. 319. Chapmand and Hall, London, U.K., 1993.
7. P. E. D. Morgan and D. B. Marshall, "Cermic Composites of Monazite and Alumina," J. Am. Ceram. Soc., 78 [6] 1553-63 (1995).
8. T. T. King and R. F. Cooper, "Ambient-Temperature Mechanical Response of Alumina-Fluoromica Laminates," J. Am. Ceram. Soc., 77 [7] 1699-705 (1994).
9. S. R. Nutt, "Environmental Effects on Mechanical Behavior of Ceramics"; pp. 365-406 in High Temperature Mechanical Behavior of Ceramic Composites. Edited by S. V. Nair and K. Jakus. Butterworth-Heinemann, Newton, MA, 1995.
10. J. B. Davis, J. P. A. Löfvander, A. G. Evans, E. Bischoff, and M. L. Emiliani, "Fiber Coating Concepts for Brittle-Matrix Composites," J. Am. Ceram. Soc., 76 [5] 1249-63 (1993).
11. K. S. Blanks, A. Kristoffersson, E. Carlström, and W. J. Clegg, "Crack Deflection in Ceramic Laminates Using Porous Interlayers," J. Eur. Ceram. Soc., 18, 1945-91 (1998).
12. M. Y. He and J. W. Hutchinson, "Crack Deflection at an Interface Between Dissimilar Elastic Materials," Int. J. Solids Struct., 25 [9] 1053-67 (1989).
13. Coors Ceramic Company, Golden, CO.
14. "MIL-STD-1942A: Flexural Strength of High Performance Ceramic at Ambient Temperature," Department of the Army, Washington, DC, 1990.
15. P. G. Charalambides, J. Lund, A. G. Evans, and R. M. McMeeking, "A Test Specimen for Determining the Fracture Resistance of Bimaterial Interfaces," J. Appl. Mech., 56, 77-82 (1989).
16. A. G. Evans, M. Linzer, and L. R. Russell, "Acoustic Emission and Crack Propagation in Polycrystalline Alumina," Mater. Sci. Engng., 15, 253-61 (1974).
17. Ic," Proc. Br. Ceram. Soc., 25, 139-49 (1975).
18. J. C. Jaeger and N. G. W. Cook, Fundamentals of Rock Mechanics. Chapmand and Hall, London, U.K., 1979.
19. W. Chen and G. Ravichandran, "Dynamic Compresseve Failure of a Glass Ceramic under Lateral Confinement," J. Mech. Phys. Solids, 45, 1303-28 (1997).
20. S. Satapathy and S. Bless, "Calculation of Penetration Resistance of Brittle Materials using Spherical Cavity Expansion Analysis," Mech. Mater., 23, 323-30 (1996).
21. J. Lubliner, Plasticity Theory; p. 132. Macmillan, New York, 1990.
22. A. G. Evans and G. Tappin, "Effects of Microstructure on the Stress to Propagate Inherent Flaws," Proc. Br. Ceram. Soc., 20, 275-97 (1972).
23. S. Baskaran and J. W. Halloran, "Fibrous Monolithic Ceramics: II, Flexural Strength and Fracture Behavior of the Silicon Carbide/Graphite System," J. Am. Ceram. Soc., 76, 2217-24 (1993).
24. S. Baskaran and J. W. Halloran, "Fibrous Monolithic Ceramics: III, Mechanical Properties and Oxidation Behavior of the Silicon Carbide/Boron Nitride System," J. Am. Ceram. Soc., 77, 1249-55 (1994).
25. 3," J. Am. Ceram. Soc., 56, 153-57 (1973).
26. 3): 1, Interface-Controlled Diffusional Creep," J. Am. Ceram. Soc., 63 [1] 46-53 (1980).
27. A. S. Argon and D. G. Bailey, "Failure in Laminates in Tension Under Increasing Stress, Constant Stress, and Cyclic Stress," J. Mater. Sci., 9, 201-11 (1974).
28. M. Ibnabdeljalil and W. A. Curtin, "Strength and Reliability of Fiber-Reinforced Composites: Localized Load Sharing and Associated Size Effects," Int. J. Solids Struct., 34, [21] 2649-68 (1997).