Fatigue strength of Inconel 718 at elevated temperatures

Fatigue and Fracture of Engineering Materials and Structures

Volumn 23, Issue 3, 2000, Pages 209-216

  Kawagoishi, N ^b   Chen, Q ^b   Nisitani, H ^a  

^a KYUSHU SANGYO UNIVERSITY   (Japan)

^b KAGOSHIMA UNIVERSITY   (Japan)

Author keywords

[No Author keywords available]

Indexed keywords

BENDING STRENGTH; CRACK INITIATION; CRACK PROPAGATION; FATIGUE OF MATERIALS; NICKEL ALLOYS; THERMAL EFFECTS;

ROTARY BENDING FATIGUE;

SUPERALLOYS;

EID: 0034430296     PISSN: 8756758X     EISSN: None     Source Type: Journal    
DOI: 10.1046/j.1460-2695.2000.00263.x     Document Type: Article

References (22)

1. T. M. Maccagno, A. K. Koul, J. P. Immarigeon, L. Cutler, R. Allem and G. L'esperance (1990) Microstructure, creep properties, and rejuvenation of service-exposed alloy 713C turbine blades. Metall. Trans. A 21A, 3115-3125.
2. C. W. Brown and M. A. Hicks (1982) Fatigue growth of surface cracks in nickel-based superalloys. Int. J. Fatigue 4, 73-81.
3. M. A. Burke and C. G. Beck (1984) The high temperature low-cycle fatigue behavior of the nickel base alloy IN-617. Metall. Trans. A 15A, 661-670.
4. M. Y. Nazmy and R. F. Singer (1985) High cycle fatigue and fatigue crack growth of the oxide dispersion strengthened alloy MA 7 54. Metall. Trans. A 16A, 1437-1444.
5. V. Singh, M. Sundararaman, W. Chen and R. P. Wahi (1991) Low-cycle fatigue behavior of Nimonic PE16 at room temperature. Metall. Trans. A 22A, 499-505.
6. R. R. Stephens, L. Grabowski and D. W. Hoeppner (1995) The effect of temperature on the behavior of short fatigue cracks in Waspaloy using an in situ SEM fatigue apparatus. Int. J. Fatigue 15, 273-282.
7. E. Andrieu and J. P. Henon (1987) Effect of the environment on the high temperature embrittlement of Inconel 718. Mater. Sci. Engng 88, 191-197.
8. M. Yoshiba, O. Miyagawa and H. Fujishiro (1974) Effect of grain size and notch on high cycle fatigue strength of a nickel-base superalloy at elevated temperature. Trans. Japan Soc. Mech. Engng (in Japanese) 50A, 1443-1452.
9. M. Goto, D. M. Knowles, N. Kawagoishi, H. Nisitani, T. Yakushiji and T. Yamamoto (1997) Four point bending fatigue property of Ni-base superalloy Udimet 720Li. J. Soc. Mater. Sci., Japan (in Japanese) 46, 1389-1395.
10. M. Okazaki, T. Imai, T. Satoh and S. Nohmi (1992) Fatigue small crack growth in a single crystal Ni-base superalloy at elevated temperature. J. Soc. Mater. Sci., Japan (in Japanese) 41, 1261-1267.
11. M. Okazaki, Y. Yamazaki and K. Tukuda (1996) Effect of microstructure of high-cycle fatigue strength of an oxide dispersion strengthened Ni-base superalloy at high temperatures. In: Preprints of Japan Soc. Mech. Engng (in Japanese), Vol. 96-1, Tokyo, pp. 444-445.
12. J. L. Yuen, P. Roy and W. D. Nix (1984) Effect of oxidation kinetics on the near threshold fatigue crack growth behavior of a nickel base superalloy. Metall. Trans. A 15A, 1769-1775.
13. M. Reger and L. Remy (1988) Fatigue oxidation interaction in IN 100 superalloy. Metall. Trans. A 19A, 2259-2268.
14. yγ′-strengthened alloy under low-cycle fatigue. Metall. Trans. A 20A, 2793-2801.
15. H. Sueyoshi, K. Hamaishi, T. Shiomizu and Y. Ohzono (1997) Effect of preheating in air on gas nitriding of SUS304 stainless steel. Mater. Trans. JIM 38, 616-623.
16. K. J. Miller (1991) Metal fatigue, past, current and future. In: The 27th John Plater Lecture, Proc. Instn. Mech. Engrs., London, Vol. 205 (5), pp. 291-304.
17. K. Kanazawa and S. Nishijima (1997) Fatigue fracture of low alloy steel at ultra-high-cycle region under elevated temperature condition. J. Soc. Mater. Sci., Japan (in Japanese) 46, 1396-1401.
18. N. Kawagoishi, Y. Ozono, Q. Chen, M. Goto, H. Tanaka and E. Kondo (1997) Effect of oxide films on a fatigue crack initiation and its early growth of Ni-base super alloy. J. Soc. Mater. Sci., Japan (in Japanese) 64, 839-844.
19. M. Lenglet, R. Guillamet, J. Lopitaux and B. Hannoyer (1990) Initial stages of oxidation of Inconel 718 by FTIR spectroscopy. Mater. Res. Bull. 25, 715-722.
20. W. Elber (1970) Fatigue crack closure under cyclic tension. Engng Fracture Mech. 2, 37-45.
21. R. O. Ritchie (1988) Mechanisms of fatigue crack propagation 7n metals, ceramics and composites: role of crack tip shielding. Mater. Sci. Engng 103, 15-28.
22. S. Suresh, G. F. Zamiski and R. O. Ritchie (1981) Oxide-induced crack closure: an explanation for near-threshold corrosion fatigue crack growth behavior. Metall. Trans. A 12A, 1435-1443.