Effect of microstructure on the morphology of fatigue cracks in UDIMET 720

Fatigue and Fracture of Engineering Materials and Structures

Volumn 23, Issue 9, 2000, Pages 725-736

  Brooks, R R ^a,b   Rainforth, W M ^a  

^a UNIVERSITY OF SHEFFIELD   (United Kingdom)

^b Wyman Gordon Ltd   (United Kingdom)

Author keywords

[No Author keywords available]

Indexed keywords

CRACKS; CRYSTAL MICROSTRUCTURE; FRACTURE MECHANICS; GRANULAR MATERIALS; MORPHOLOGY; SHEAR STRENGTH; STRAIN;

LOW CYCLE FATIGUE (LCF); SHEAR FRACTURES;

FATIGUE OF MATERIALS;

EID: 0034429938     PISSN: 8756758X     EISSN: None     Source Type: Journal    
DOI: 10.1046/j.1460-2695.2000.00339.x     Document Type: Article

References (19)

1. R. R. Brooks, W. M. Rainforth and L. Grabowski (1995) Fatigue damage mechanisms associated with 'tear-drop' Cracking in Udimet 720. Proceedings of the 7th International Conference on Mechanical Behaviour of Materials, June 1995, The Hague, The Netherlands (ed. A. Bakker). Delft University Press, Delft, The Netherlands, pp. 69-71.
2. R. R. Brooks and W. M. Rainforth (1999) Fatigue damage mechanisms associated with 'tear drop' cracking in Udimet 720. Fatigue Fract. Engng Mater. Struct. 22, 821-829.
3. R. R. Brooks (1996) Fatigue damage mechanisms in the nickel-based superalloy Udimet® 720. PhD Thesis, The University of Sheffield, Sheffield, UK.
4. M. Loo-Morrey and P. A. S. Reed (2000). Materials Sci. Technol. 16, 133-146.
5. A. C. Pickard (1986) Stress Intensity Solutions for Planar Crack in 3-Dimensional Bodies. Engineering Metals Advisory Service, Cradley Heath, UK, pp. 132-138.
6. W. J. Mills and L. A. James (1980) Effect of temperature on the fatigue-crack propagation behaviour of Inconel X-750. Fatigue Fract. Engng Mater. Struct. 3, 159-175.
7. K. Sadananda and P. Shahinian (1981) Analysis of Crystallographic High Temperature Fatigue Crack Growth in a Nickel Base Alloy. Metall. Trans. A 12A, 343-351.
8. J. E. King (1987) Fatigue crack propagation in nickel-base superalloys - effects of microstructure, load ratio, and temperature. Mater. Sci. Technical 3, 750-764.
9. C. W. Brown and M. A. Hicks (1982) Fatigue growth of surface cracks in nickel-based superalloys. Int. J. Fat. 4, 73-81.
10. W. M. Rainforth, J. Nutting and R. Stevens (1992) Deformation structure induced by sliding contact. Phil. Magazine 66, 621-641.
11. M. G. Castelli, R. V. Miner and D. N. Robinson (1993) Thermomechanical deformation behaviour of a dynamic strain ageing alloy, Hastelloy X™. Thermomechanical Fatigue Behavior of Materials, ASTM STP 1186. (ed. H. Sehitoglu). ASTM, Philadelphia, PA, USA, 106-125.
12. T. A. Bloom, U. F. Kocks and P. Nash (1985) Deformation behaviour of Ni-Mo alloys. Acta Metall. 33, 265-272.
13. H. Nahm and J. Moteff (1976) Second phase formation and its influence on the fatigue properties of Incoloy 800 at elevated temperatures. Metall. Trans. A 7A, 1473-1477.
14. R. A. Venables and J. E. King (1984) The effects of dynamic strain ageing on fatigue crack propagation and threshold behaviour in a Ni-base superalloy. Fatigue '84, 2nd International Conference on Fatigue. EMAS, Warley, UK, pp. 1371-1378.
15. R. V. Miner and M. G. Castelli (1992) Hardening mechanisms in a dynamic strain aging alloy, Hastelloy X, during isothermal and thermomechanical cyclic deformation. Metall. Trans. A 23A, 551-561.
16. R. A. Mulford and U. F. Kocks (1979) New observations on the mechanisms of dynamic strain aging and of jerky flow. Acta Metall. 27, 1125-1134.
17. J. E. King, C. P. You and J.F. Knott (1981) Serrated yielding and the localized shear failure mode in aluminium-alloys. Acta Metall. 29, 1553-1566.
18. S. Kumar (1995) Inverse behaviour of the onset strain serrated flow. Scripta Metall. 33, 81-86.
19. N. S. Stoloff (1990) Wrought and P/M superalloys. Metals Handbook. Vol. 1. Properties and Selection. ASTM, Philadelphia, PA, USA, pp. 950-62.