Probabilistic approach to predict the very high-cycle fatigue behaviour of spheroidal graphite cast iron structures

Fatigue and Fracture of Engineering Materials and Structures

Volumn 23, Issue 2, 2000, Pages 173-180

  Chantier, I ^a   Bobet, V ^b   Billardon, R ^a   Hild, F ^a  

^a SORBONNE UNIVERSITÉ   (France)

^b RENAULT   (France)

Author keywords

[No Author keywords available]

Indexed keywords

EXTRAPOLATION; FAILURE (MECHANICAL); FATIGUE TESTING; GRAPHITE; METAL CASTING; PROBABILITY; STRESS ANALYSIS; STRUCTURAL ANALYSIS;

CASTING FLAW DISTRIBUTIONS; STRESS HETEROGENEITY EFFECT;

CAST IRON;

EID: 0034427412     PISSN: 8756758X     EISSN: None     Source Type: Journal    
DOI: 10.1046/j.1460-2695.2000.00228.x     Document Type: Article

References (13)

1. S.-H. Dai and M. O. Wang (1992) Reliability Analysis in Engineering Applications, Van Norstrand Rheinhold, New York, USA.
2. A. M. Freudenthal (1968) Statistical approach to brittle fracture. In: Fracture (Edited by H. Liebowitz), Academic Press, New York, USA, Vol. 2, pp. 591-619.
3. F. Hild and D. Marquis (1992) A statistical approach to the rupture of brittle materials. Eur. J. Mech. A/Solids 11, 753-765.
4. P. Clément, J.-P. Angeli and A. Pineau (1984) Short crack behaviour in nodular cast iron. Fatigue Engng Mater. Struct. 7, 251-265.
5. J. Pellas, G. Baudin and M. Robert (1977) Mesure et calcul du seuil de fissuration après surcharge. Recherche Aérospatiale 3, 191-201.
6. H. Yaacoub Agha, A.-S. Béranger, R. Billardon and F. Hild (1998) High-cycle fatigue behaviour of spheroidal graphite cast iron. Fatigue Fract. Engng Mater. Struct. 21, 287-296.
7. K. J. Miller (1993) The two thresholds of fatigue behaviour. Fatigue Fract. Engng Mater. Struct. 16, 931-939.
8. Y. Nadot, N. Raganathan, J. Mendez and A.-S. Béranger (1997) A study of natural cracks initiated on casting defects by crack front marking. Scripta Mater. 37, 549-553.
9. K. J. Miller and R. Akid (1996) The application of microstructural fracture mechanics to various metal surface states. Proc. R. Soc. Lond. A 452, 1411-1432.
10. W. H. Press, S. A. Teukolsky, W. T. Vetterling and B. P. Flannery (1992) Numerical Recipes in Fortran, Cambridge University Press, Cambridge, USA.
11. V. Kadlecek and Z. Spleta (1967) Effect of size and shape of test specimens on the direct tensile strength of concrete. Bull. RILEM 36, 175-184.
12. S. L'Hermite (1973) Influence de la dimension absolue sur la résistance de flexion. Annales l'ITBTB 309-310, 39-41.
13. Y. Katamaya and Y. Hattory (1982) Effects of specimen size on strength of sintered silicon nitride. C. J. Am. Ceram. Soc. 65, C-164-C-165.