Fretting fatigue of zinc coated low carbon steel EN H320 M

Tribology International

Volumn 33, Issue 11, 2000, Pages 761-768

  Ramalho, A ^a   Correia, L M ^a   Costa, J D ^a  

^a UNIVERSITY OF COIMBRA   (Portugal)

Author keywords

[No Author keywords available]

Indexed keywords

CARBON STEEL; DEGRADATION; FATIGUE TESTING; FRACTURE; METALLIC FILMS; PROTECTIVE COATINGS; SCANNING ELECTRON MICROSCOPY; WEAR OF MATERIALS; ZINC;

FRETTING FATIGUE;

STEEL SHEET;

EID: 0034320918     PISSN: 0301679X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0301-679X(00)00119-5     Document Type: Article

References (18)

1. Fenner A.J., Field J.E. La fatigue dans les conditions de frottement. Rev. Métall. 55:1958;478-485.
2. Nowell D., Hills D.A. Crack initiation criteria in fretting fatigue. Wear. 136:1990;329-343.
3. Fellows L.J., Nowell D., Hills D.A. On the initiation of fretting fatigue cracks. Wear. 205:1997;120-129.
4. Fouvry S., Kapsa Ph., Vincent L., Dang Van K. Theoretical analysis of fatigue cracking under dry friction for fretting loading conditions. Wear. 195:1996;21-34.
5. Takaji M., Hasan M. Changes in surface texture of zinc-coated steel sheets under plastic deformation. Wear. 198:1996;176-184.
6. Takaji M., Hasan M. Contact mechanics of zinc-coated steel sheets. Wear. 199:1996;260-267.
7. ISO 13565-2:1996 Geometrical Product Specifications (GPS) - Surface texture: Profile method; Surfaces having stratified functional properties - Part 2: Height characterization using the linear material ratio curve.
8. Leis B. Fatigue and Fracture. ASM Handbook. Fatigue and Fracture. vol. 19:1996;314-320.
9. Reeves R.K., Hoeppner D.W. The effect of fretting on fatigue. Wear. 40:1976;395-397.
10. Endo K., Goto H. Initiation and propagation of fretting fatigue cracks. Wear. 38:1976;311-324.
11. Wharton M.H., Taylor D.E., Waterhouse R.B. Metallurgical factors in fretting fatigue behavior of 70/30 brass and 0.7% carbon steel. Wear. 23:1973;251-260.
12. Ruiz C., Boddington P.H.B., Chen K.C. An investigation of fatigue and fretting in a dovetail joint. Exp. Mech. 24(3):1984;208-217.
13. Nowell D., Hills D.A. Crack initiation criteria in fretting fatigue. Wear. 136:1990;329-343.
14. Adibnazari S., Hoeppner D.W. A fretting fatigue normal pressure threshold concept. Wear. 160:1993;33-35.
15. Vingsbo O., Soderberg S. On fretting maps. Wear. 126:1988;131-147.
16. Mindlin R.D., Deresiewicz H. Elastic spheres in contact under varying oblique forces. J. Appl. Mech. 75:1953;327-344.
17. Gao H., Gu H., Zhou H. Effect of slip amplitude on fretting fatigue. Wear. 148:1991;15-23.
18. Koul A.K., Xue L., Wallace W., Bibby M., Chakravarty S., Andrews R.G., Patnaik P.C. An investigation on surface treatments for improving the fretting fatigue resistance of titanium alloys. Proceedings of the 82nd Meeting of AGARD/SMB, Sesimbra. 1996;5.1-5.9.