Mixed-mode, high-cycle fatigue-crack growth thresholds in Ti-6A1-4V II. Quantification of crack-tip shielding

Engineering Fracture Mechanics

Volumn 67, Issue 3, 2000, Pages 229-249

  Campbell, J P ^a   Ritchie, R O ^a  

^a Lawrence Berkeley National Laboratory   (United States)

Author keywords

Crack tip shielding; Fatigue thresholds; High cycle fatigue; Mixed mode

Indexed keywords

CRACK INITIATION; CRACK PROPAGATION; FATIGUE OF MATERIALS; FRACTURE MECHANICS; METALLOGRAPHIC MICROSTRUCTURE; SHEAR STRESS; STRESS ANALYSIS; STRESS CONCENTRATION; TENSILE TESTING;

CRACK-TIP SHIELDING; HIGH-CYCLE FATIGUE (HCF);

TITANIUM ALLOYS;

BLADE; CRACK PROPAGATION; FATIGUE; RESISTANCE; TURBINE;

EID: 0034307828     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0013-7944(00)00047-3     Document Type: Article

References (43)

1. High cycle fatigue in aircraft gas turbines - an industry perspective
2. On the use of the Goodman diagram for high cycle fatigue design
3. Mixed-mode fatigue thresholds
4. Growth of fatigue cracks under combined mode I and mode II loads
5. Fatigue crack propagation in titanium under general in-plane loading - I: Experiments
6. Fatigue crack propagation in titanium under general in-plane loading - II: Analysis
7. Fatigue crack propagation from a crack inclined to the cyclic tensile axis
8. The influence of precracking techniques on fatigue crack growth thresholds under mixed mode I/II loading conditions
9. The significance of mean stress on the fatigue crack growth threshold for mixed mode I + II loading
10. Mixed-mode I and II fatigue threshold and crack closure in dual-phase steels
11. Crack-propagation rate in 7075-T6 plates under cyclic tensile and transverse shear loading
12. Near-threshold crack growth behavior of a single crystal Ni-base superalloy subjected to mixed mode loading
13. High-cycle fatigue of Ti-6A1-4V
14. Mixed-mode, high-cycle fatigue-crack growth thresholds in Ti-6A1-4V. Part I. A comparison of large- and short-crack behavior
15. Mixed-mode fracture: The four-point shear specimen
16. Asymmetric four-point crack specimen
17. Mixed-mode fracture toughness of ceramic materials
18. A 1 kHz servohydraulic fatigue testing system
19. Fatigue crack closure under cyclic tension
20. Short crack effects in fatigue: A consequence of crack tip shielding
21. A failure mechanism map for mixed mode I and II fatigue crack growth threshold
22. Mixed-mode I and II fatigue threshold and crack deflection angle in SiCp/2024A1 composite
23. Toward an understanding of mode II fatigue crack growth
24. The formation and propagation of mode I branch cracks in mixed mode fatigue failure
25. Effects of friction and high torque on fatigue crack propagation in mode III
26. Sliding mode crack closure and mode III fatigue crack growth in mild steel
27. A model for sliding mode crack closure. I. Theory for pure mode II loading
28. A model for sliding mode crack closure. II. Mixed mode I and II loading and application
29. A mixed mode fatigue crack closure model
30. Fatigue crack propagation in ARALL laminates: Measurement of the effect of crack-tip shielding from crack bridging
31. The effect of microstructure on fracture toughness and fatigue crack growth behavior in γ-titanium aluminide based intermetallics
32. Perspective on the development of high-toughness ceramics
33. Micromechanics of shear ligament toughening
34. Ductile-reinforcement toughening in γ-TiAl intermetallic-matrix composites: Effects on fracture toughness and fatigue-crack propagation resistance
35. Thresholds for high-cycle fatigue in a turbine engine Ti-6Al-4V alloy
36. Fatigue crack growth in metals and alloys: Mechanisms and micromechanics
37. Studies on cyclic crack path and the mixed mode crack closure behavior in Al-alloy
38. A geometric model for fatigue crack closure induced by fracture surface morphology
39. Threshold for fatigue crack propagation and effects of load ratio and frequency
40. The influence of plasticity on mixed-mode interface toughness