Experimental apparatus for thermal shock fatigue investigations

International Journal of Pressure Vessels and Piping

Volumn 77, Issue 7, 2000, Pages 425-434

  Kerezsi, B B ^a   Kotousov, A G ^a   Price, J W H ^a  

^a MONASH UNIVERSITY   (Australia)

Author keywords

Crack growth; Fatigue; Pressure equipment; Primary load; Test rig; Thermal shock

Indexed keywords

CRACK INITIATION; CRACK PROPAGATION; LIFE CYCLE; STRESS CONCENTRATION; STRUCTURAL LOADS; THERMAL CYCLING; WELDS;

THERMAL SHOCK;

PRESSURE VESSELS;

CRACK PROPAGATION; FATIGUE ANALYSIS; PIPING; PRESSURE VESSEL; SHOCK; TEST RIG;

EID: 0034281562     PISSN: 03080161     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0308-0161(00)00025-9     Document Type: Article

References (31)

1. Apparatus for study of effects of cyclic thermal stresses on ductile metals
2. Thermal effect on low cycle fatigue strength of steels. Thermal stresses and thermal fatigue
3. Low-cycle fatigue with combined thermal and strain cycling
4. Evaluation of thermal fatigue resistance of metals using the fluidized bed technique
5. Some contributions to British work on thermal and high strain fatigue. Thermal stresses and thermal fatigue
6. Thermal-mechanical fatigue crack propagation in nickel- and cobalt-base superalloys under various strain-temperature cycles
7. Thermal fatigue characterization of cast cobalt and nickel-base superalloys
8. Crack initiation and growth during thermal cycling
9. Thermomechanical fatigue crack propagation in an anisotropic (directionally solidified) nickel-base superalloy
10. Thermal cycling apparatus for thermomechanical fatigue testing
11. Thermal fatigue of a 12% chromium martensitic stainless steel
12. Thermal fatigue of steel tires on urban railway systems
13. The influence of environment on fatigue
14. Effect of microstructure on the thermal fatigue resistance of a cast cobalt-base alloy, Mar-M509
15. Thermal shock fracture experiments on large size plates of A533-B steel
16. Initiation and growth of cracks under thermal fatigue loading for a 316L type steel. Fatigue under thermal and mechanical loading: Mechanisms, mechanics and modelling
17. Crack growth under cyclic thermal shock loading
18. Effects of mean load on creep and fatigue crack growth at elevated temperature
19. Stress intensity factors for axial cracks in hollow cylinders subjected to thermal shock
20. Thermal shock of a pipe with a partly circumferential surface crack
21. Thermal fatigue behaviour of T-111 and ASTAR 811C in ultrahigh vacuum
22. Retarding the crack initiation process during low cycle thermal shock fatigue. Low cycle fatigue and elasto-plastic behaviour of materials
23. A thermal-mechanical fatigue crack-growth testing system
24. Comparison of theoretical estimates and experimental measurements of fatigue crack growth under severe thermal shock conditions-Part 1: Experimental observations
25. Relationship between crack growth of thermal mechanical fatigue and that of isothermal low-cycle fatigue at elevated temperatures. Low cycle fatigue and elasto-plastic behaviour of materials
26. Notch fatigue crack initiation in high temperature water environments: Experiments and life prediction