Volumn 243, Issue 1-2, 2000, Pages 167-174

The influence of ring crack location on the rolling contact fatigue failure of lubricated silicon nitride: Fracture mechanics analysis

(2) Wang, Y a Hadfield, M a

a BOURNEMOUTH UNIVERSITY (United Kingdom)

Author keywords

Boundary element method; Ring crack propagation; Rolling contact fatigue

Indexed keywords

BOUNDARY ELEMENT METHOD; COMPUTATIONAL METHODS; CRACK PROPAGATION; FAILURE ANALYSIS; FATIGUE OF MATERIALS; FRACTURE MECHANICS; FRACTURE TESTING; LOAD TESTING; LUBRICATION; MATHEMATICAL MODELS; STRESS ANALYSIS; STRESS INTENSITY FACTORS;

ROLLING CONTACT TESTS;

SILICON NITRIDE;

CRACK DETECTION; FATIGUE; LUBRICATION; ROLLING CONTACT; WEAR;

EID: 0034253526 PISSN: 00431648 EISSN: None Source Type: Journal
DOI: 10.1016/S0043-1648(00)00436-1 Document Type: Article

Times cited : (37)

References (19)

1
- 0042529326
- Rolling element bearings into the 21st century
- (1990) Proceedings of IMechE Seminar, London
- Cundill, R.T.¹

2
- 0017522719
- Mechanics of crack propagation in delamination wear
- (1977) Wear , vol.44 , pp. 39-56
- Fleming, J.R.¹ Suh, N.P.²

3
- 0020159803
- Subsurface and surface cracking due to Hertzian contact
- (1982) J. Lubrication Technol. Trans. ASME , vol.104 , pp. 347-351
- Keer, L.M.¹ Bryant, M.D.² Haritos, G.K.³

4
- 0022465539
- Mechanism of surface crack growth in lubricated rolling sliding spherical contact
- (1986) Trans. ASME , vol.53 , pp. 354-360
- Kaneta, M.¹ Suetsugu, M.² Murakami, Y.³

5
- 0026805609
- An analytical life prediction model for the crack propagation occurring in contact fatigue failure
- (1992) ASLE Trans. , vol.35 , pp. 451-461
- Hanson, M.T.¹ Keer, L.M.²

6
- 0020737315
- A pitting model for rolling-contact fatigue
- (1983) J. Lubrication Technol. Trans. ASME , vol.105 , pp. 198-205
- Keer, L.M.¹ Bryant, M.D.²

7
- 0024092028
- The influence of crack face friction and trapped fluid on surface initiated rolling-contact fatigue cracks
- (1988) J. Tribol. Trans. ASME , vol.110 , pp. 704-711
- Bower, A.F.¹

8
- 0021892056
- Analysis of surface crack-propagation in lubricated rolling-contact
- (1985) ASLE Trans. , vol.28 , pp. 60-68
- Murakami, Y.¹ Kaneta, M.² Yatsuzuka, H.³

9
- 0028468853
- Three-dimensional fracture mechanics analysis of pit formation mechanism under lubricated rolling sliding contact loading
- (1994) ASLE Trans. , vol.37 , pp. 445-454
- Murakami, Y.¹ Sakae, C.² Inchimaru, K.³

10
- 0027607766
- Failure modes of ceramic elements with ring-crack defects
- (1993) Tribol. Int. , vol.26 , pp. 157-164
- Hadfield, M.¹ Stolarski, T.A.² Cundill, R.T.³ Horton, S.⁴

11
- 0027677327
- Failure modes of pre-cracked ceramic elements under rolling-contact
- (1993) Wear , vol.169 , pp. 69-75
- Hadfield, M.¹ Stolarski, T.A.² Cundill, R.T.³ Horton, S.⁴

12
- 0034253212
- The influence of ring crack location on the rolling contact fatigue failure of lubricated silicon nitride: Experimental studies
- (2000) Wear , vol.243 , pp. 158-167
- Wang, Y.¹ Hadfield, M.²

13
- 85040875608
- Cambridge University Press, Cambridge
- (1985) Contact Mechanics
- Johnson, K.L.¹

14
- 0031922501
- Crack face friction effects on mode II stress intensities for a surface-cracked coating in two-dimensional rolling contact
- (1998) Tribol. Trans. , vol.41 , pp. 35-42
- Eberhardt, A.W.¹ Kim, B.S.²

15
- 0008119903
- in H. Kitagawa and T. Tanaka (Eds.); Edgbaston, UK
- (1990) Fatigue 90: Proceedings of 4th International Conference on Fatigue and Fatigue Thresholds, Vol. 2, Mat. Comp. Eng. Publ., Ltd. , pp. 793-798
- Bar-On, I.¹ Beals, J.T.²

16
- 0016351409
- A fracture criterion for three-dimensional crack problems
- (1974) Eng. Fracture Mech. , vol.6 , pp. 699-723
- Sih, G.C.¹ Cha, B.C.K.²

17
- 0029378774
- Behaviour of cyclic fatigue cracks in monolithic silicon nitride
- (1995) J. Am. Ceram. Soc. , vol.78 , pp. 2291-2300
- Gilbert, C.J.¹ Dauskardt, R.H.² Ritchie, R.O.³

18
- 0026244135
- Cyclic fatigue of ceramics - a fracture-mechanics approach to subcritical crack-growth and life prediction
- (1991) Nippon Seramikkusu Kyokai Gakujutsu Ronbunshi-J. Ceram. Soc. Jpn. , vol.99 , pp. 1047-1062
- Ritchie, R.O.¹ Dauskardt, R.H.²

19
- 0004318384
- submitted for publication
- (2000) Mechanisms of Ceramic Ring Crack Failure in Lubricated Rolling Contact
- Wang, Y.¹ Hadfield, M.²

* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.