Interface crack interacting with a microvoid in the near-tip process zone

International Journal of Fracture

Volumn 102, Issue 3, 2000, Pages 223-244

  Han, J J ^a   Chen, Y H ^a  

^a XI'AN JIAOTONG UNIVERSITY   (China)

Author keywords

Interaction; Interface; J integral; Macrocrack; Microvoid; Shielding

Indexed keywords

INTEGRAL EQUATIONS; INTERFACES (MATERIALS); MICROCRACKS; PROBLEM SOLVING;

MICROVOIDS; NEAR-TIP PROCESS ZONES; PSEUDOTRACTION EDGE DISLOCATION METHOD;

FRACTURE MECHANICS;

FRACTURE MECHANICS;

EID: 0034173878     PISSN: 03769429     EISSN: None     Source Type: Journal    
DOI: 10.1023/A:1007479717979     Document Type: Article

References (25)

1. On the contribution of discontinuities in the near-tip stress field to J-integral
2. Elastic interaction of a crack with a microcrack array - Part I and Part II
3. Discussion of a paper by D.B. Bogy
4. On the numerical solution of singular integral equations
5. Crack path selection in a brittle adhesive layer
6. General solution to the problem of microcracks near the tip of a main crack
7. On the effect of the release of residual stress duo to near-tip microcracking
8. On energy release rates for a plane crack
9. Interacting microcrack near the tips in the process zone of a macro crack
10. Crack-tip shielding by micro cracking in brittle solids
11. Crack paralleling an interface between dissimilar materials
12. Distributed crack and kinked cracks in bonded dissimilar half planes with an interface crack
13. A continuum theory of crack shielding in ceramics
14. Maximal crack-tip shielding by microcracking
15. A path-independent integral and the approximation analysis of strain concentration by notches and cracks
16. Elastic fracture mechanics concepts for interfacial cracks
17. Microcrack interaction with a main crack
18. Macrocrack-microdefect interaction
19. Singularities interacting with interface and cracks
20. The stress around a fault or crack in dissimilar media
21. Interaction of a semi-infinite crack and a parallel subinterface rack
22. On the contribution of subinterface microcracks near the tip of an interface macrocrack to the J-integral in bimaterial solids