Fracture mechanics analysis of coating/substrate systems: Part I: Analysis of tensile and bending experiments

Engineering Fracture Mechanics

Volumn 65, Issue 5, 2000, Pages 573-593

  Kim, Sung Ryong ^a   Nairn, John A ^a  

^a UNIVERSITY OF UTAH   (United States)

Author keywords

Coatings; Fracture mechanics; Paints; Variational mechanics

Indexed keywords

BENDING (DEFORMATION); COATINGS; FRACTURE TOUGHNESS; MICROCRACKS; STRAIN; TENSILE TESTING;

BENDING LOADS; TENSILE LOADS; VARIATIONAL MECHANICS;

FRACTURE MECHANICS;

COATING; FRACTURE MECHANICS; PAINT;

EID: 0034056662     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0013-7944(99)00141-1     Document Type: Article

References (30)

1. Nairn J.A., Kim S.R. A fracture mechanics analysis of multiple cracking in coatings. Eng. Fract. Mech. 42:1992;195-208.
2. Kim SR. Fracture mechanics approach to multiple cracking in paint films. M.S. Thesis, University of Utah, 1989.
3. Kim SR. Understanding cracking failures of coatings: a fracture mechanics approach. Ph.D. Thesis, University of Utah, 1993.
4. So P., Broutman L.J. The effect of surface embrittlement on the mechanical behavior or rubber-modified polymers. Polym. Engng. Sci. 22:1982;888-894.
5. Rolland L., Broutman L.J. Surface embrittlement of ductile polymers: a fracture mechanics analysis. Polym. Engng. Sci. 25:1985;207-211.
6. So P.K., Broutman L.J. The fracture behavior or surface embrittled polymers. Polym. Engng. Sci. 26:1986;1173-1179.
7. Crouch B.A. The mechanics of surface embrittlement of polymers. Materials and mechanics issues. 1993;339-350 ASME, New York.
8. Verpy C., Gacougnolle J.L., Dragon A., Vanlerberghe A., Chesneau A., Cozette F. The surface embrittlement of a ductile blend due to a brittle paint layer. Progress in Organic Coatings. 24:1994;115-129.
9. Hsieh A.J., Huang P., Venkataraman S.K., Kohlstedt D.L. Mechanical characterization of diamond-like carbon (DLC) coated polycarbonates. Mat. Res. Cos. Symp. Proc. 308:1993;653-658.
10. Tensile properties of organic coatings. ASTM D-2370, 1982.
11. Paint testing manual. In: Sward GG, editor. ASTM STP 500, 1972.
12. Durelli A.J., Phillips E.A., Tsao C.H. Properties of stress coat. Analysis of stress and strain. 1958;375-431 McGraw-Hill, New York.
13. Kim SR, Nairn JA. Fracture mechanics analysis of coating/substrate systems. Part II: Experiments in bending. Engr Fract Mech 2000;65:601-15 (submitted).
14. McCartney L.N., Pierce C. Stress transfer mechanics for multiple ply laminates for axial loading and bending. Proc. ICCM-11, Gold Coast, Australia :1997.
15. McCartney LN, Pierce C. Stress transfer mechanics for multiple ply laminates subject to bending. NPL Report CMMT(A)55, 1997.
16. Hashin Z. Analysis of cracked laminates: a variational approach. Mech. Mat. 4:1985;121-136.
17. Hashin Z. Analysis of stiffness reduction of cracked cross-ply laminates. Eng. Fract. Mech. 25:1986;771-778.
18. Nairn JA. The strain energy release rate of composite microcracking: a variational approach. J Comp Mat 1989;23:1106-29 (see errata: J Comp Mat 1990;24:233).
19. Nairn JA. The strain energy release rate of composite microcracking: a variational approach. J Comp Mat 1989;23:1106-29 (see errata: J Comp Mat 1990;24:233).
20. Nairn J.A., Hu S., Bark J.S. A critical evaluation of theories for predicting microcracking in composite laminates. J. Mat. Sci. 28:1993;5099-5111.
21. Nairn J.A., Hu S. Micromechanics of damage: a case study of matrix microcracking. Ramesh Talreja. Damage mechanics of composite materials. 1994;187-243 Elsevier, Amsterdam.
22. McCartney L.N. Theory of stress transfer in a 0-90-0 cross-ply laminate containing a parallel array of transverse cracks. J. Mech. Phys. Solids. 40:1992;27-68.
23. Nairn J.A. A variational mechanics analysis of the stresses around breaks in embedded fibers. Mech. Mat. 13:1992;131-154.
24. Nairn J.A. Fracture mechanics of composites with residual thermal stresses. J. Appl. Mech. 64:1997;804-810.
25. Hashin Z. Finite thermoelastic fracture criterion with application to laminate cracking analysis. J. Mech. Phys. Solids. 44:1996;1129-1145.
26. Crandall S.H., Dahl N.C., Lardner T.J. An introduction to the mechanics of solids. 1978;McGraw-Hill, New York.
27. Mathematica Version 2.2, Wolfram Research, Champaign, IL, 1994.
28. Varna J., Berglund L.A. A model for prediction of the transverse cracking strain in cross-ply laminates. J. Reinf. Plast. and Comp. 11:1992;708-728.
29. Varna J., Berglund L. Multiple transverse cracking and stiffness reduction in cross-ply laminates. J. Comp. Tech. Res. 13:1991;97-106.
30. McCartney LN. Stress transfer mechanics for ply cracks in general symmetric laminates. NPL Report CMMT(A)50, 1996.