Effect of geometry and load history on fatigue crack growth in Ti-62222

ASTM Special Technical Publication

Volumn , Issue 1372, 2000, Pages 175-191

  Liknes, Haakon O ^a   Stephens, Robert R ^a  

^a UNIVERSITY OF IDAHO   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

CRACK PROPAGATION; FATIGUE TESTING; STRESS ANALYSIS; TENSILE STRESS; TITANIUM ALLOYS;

BIAXIALITY; FATIGUE THRESHOLD; LOAD RATIO;

FATIGUE OF MATERIALS;

EID: 0033899884     PISSN: 10403094     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1520/stp13433s     Document Type: Conference Paper

References (24)

1. Liu, A. F., Allison, J. E., Dittmer, D. F., and Yamane, J. R., "Effect of Biaxial Stresses on Crack Growth," Fracture Mechanics, ASTM STP 677, C. W. Smith, Ed., American Society for Testing and Materials, 1979, pp. 5-22.
2. Leevers, P. S., Culver, L. E., and Radon, J. C., "Fatigue Crack Growth in PMMA and Rigid PVC under Biaxial Stress," Engineering Fracture Mechanics, Vol. 11, 1979, pp. 487-498.
3. Shercliff, H. R. and Fleck, N. A., "Effect of Specimen Geometry on Fatigue Crack Growth in Plain Strain - II. Overload Response," Fatigue and Fracture of Engineering Materials and Structures, Vol. 13, 1990, pp. 297-310.
4. Lang, R. W., Hahn, M. T., Hertzberg, R. W., and Manson, J. A., "Effects of Specimen Configuration and Frequency on Fatigue Crack Propagation in Nylon 66," Fracture Mechanics: Fifteenth Symposium, ASTM STP 833, R. J. Sanford, Ed., American Society for Testing and Materials, Philadelphia, 1984, pp. 266-283.
5. Horng, J. L. and Fine. M. E., "Near-threshold Fatigue Crack Propagation Rates of Dual-phase Steels," Materials Science and Engineering, Vol. 67, 1984, pp. 185-195.
6. Vecchio, R. S., Crompton, J. S., and Hertzberg, R. W., "The Influence of Specimen Geometry on Near Threshold Fatigue Crack Growth," Fatigue and Fracture of Engineering Materials and Structures, Vol. 10, 1987, pp. 333-342.
7. Saxena, V. K., Malakondaiah, G., and Radhakrishnan, V. M., "Influence of Specimen Configuration and Loading History on Fatigue Crack Growth Behaviour of 2024-T3 Clad Aluminum Alloy," Engineering Fracture Mechanics, Vol. 49, 1994, pp. 153-157.
8. Betegón, C. and Hancock, J. W., "Two-Parameter Characterization of Elastic-Plastic Crack-Tip Fields," Journal of Applied Mechanics, Vol. 58, 1991, pp. 104-110.
9. Wang, Y.-Y., "On the Two-Parameter Characterization of Elastic-Plastic Crack-Front Fields in Surface-Cracked Plates," Constraint Effects in Fracture, ASTM STP 1171, E. M. Hackett, K.-H. Schwalbe, and R. H. Dodds, Eds., American Society for Testing and Materials, 1993, pp. 120-138.
10. Sumpter, J. D. G., "An Experimental Investigation of the T Stress Approach," Constraint Effects in Fracture, ASTM STP 1171, E. M. Hackett, K.-H. Schwalbe, and R. H. Dodds, Eds., American Society for Testing and Materials, 1993, pp. 492-502.
11. Williams, M. L., "On the Stress Distribution at the Base of a Stationary Crack," Journal of Applied Mechanics, Vol. 24, 1957, pp. 109-114.
12. Rice, J. R., "Limitations to the Small Scale Yielding Approximation for Crack Tip Plasticity," Journal of Mechanics and Physics of Solids,Vol. 22, 1974, pp. 17-26.
13. Larsson, S. G. and Carlsson, A. J., "Influence of Non-Singular Stress Terms and Specimen Geometry on Small-Scale Yielding at Crack Tips in Elastic-Plastic Materials," Journal of Mechanics and Physics of Solids, Vol. 21, 1973, pp. 263-277.
14. Leevers, P. S. and Radon, J. C., "Inherent Stress Biaxiality in Various Fracture Specimen Geometries," International Journal of Fracture, Vol. 19, 1982, pp. 311-325.
15. Sherry, A. H., France, C. C., and Goldthorpe, M. R., "Compendium of T-Stress Solutions for Two and Three Dimensional Cracked Geometries," Fatigue and Fracture of Engineering Materials and Structures,Vol. 18, 1995, pp. 141-155.
16. Piascik, R. S., Newman Jr., J. C., and Underwood, J. H., "The Extended Compact Tension Specimen," Fatigue and Fracture of Engineering Materials and Structures, Vol. 20, 1997, pp. 449-563.
17. Adams, N. J. I., "Some Comments on the Effect of Biaxial Stress on Fatigue Crack Growth and Fracture," Engineering Fracture Mechanics, Vol. 5, 1973, pp. 983-991.
18. McClung, R. C., "Closure and Growth of Mode I Cracks in Biaxial Fatigue," Fatigue and Fracture of Engineering Materials and Structures, Vol. 12, 1989, pp. 447-460.
19. Joshi, S. R. and Shewchuk, J., "Fatigue-crack Propagation in a Biaxial-stress Field," Experimental Mechanics, Vol. 10, 1970, pp. 529-533.
20. Cotterell, B., "On Fracture Path Stability in the Compact Tension Test," International Journal of Fracture Mechanics, Vol. 6, 1970, pp. 189-192.
21. Kfouri, A. P., "Some Evaluations of the Elastic T-term Using Eshelby's Method," International Journal of Fracture, Vol. 30, 1986, pp. 301-315.
22. Yoder, G. R., Cooley, L. A., and Crooker, T. W., "Quantitative Analysis of Microstructural Effects on Fatigue Crack Growth in Widmanstätten Ti-6Al-4V and Ti-8Al-lMo-1V," Engineering Fracture Mechanics, Vol. 11, 1979, pp. 805-816.
23. Irving, P. E. and Beevers, C. J., "Microstructural Influences on Fatigue Crack Growth in Ti-6Al-4V," Materials Science and Engineering, Vol. 14, 1974, pp. 229-238.
24. Yuen, A., Hopkins, S. W., Leverant, G. R., and Rau, C. A., "Correlations Between Fracture Surface Appearance and Fracture Mechanics Parameters for Stage II Fatigue Crack Propagation in Ti-6Al-4V," Metallurgical Transactions, Vol. 5, 1974, pp. 1833-1842.