Volumn 197, Issue 1, 2000, Pages 197-203

Effect of specimen thickness on fatigue crack growth rate

Author keywords

[No Author keywords available]

Indexed keywords

CRACK PROPAGATION; ELASTOPLASTICITY; FRACTURE MECHANICS; NICKEL ALLOYS; STAINLESS STEEL; STEEL TESTING; STRESS INTENSITY FACTORS;

EID: 0033897118     PISSN: 00295493     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0029-5493(99)00253-8     Document Type: Article
Times cited : (50)

References (22)
  • 3
    • 84980229635 scopus 로고
    • A critical comparison of proposed parameters for high-strain fatigue crack growth
    • Brown M.W., de los Rios E.R., Miller K.J. A critical comparison of proposed parameters for high-strain fatigue crack growth. ASTM STP. 924:1988;233-259.
    • (1988) ASTM STP , vol.924 , pp. 233-259
    • Brown, M.W.1    De Los Rios, E.R.2    Miller, K.J.3
  • 4
    • 0017980933 scopus 로고
    • Analysis of closure in fatigue crack growth
    • Budiansky B., Hutchinson J.W. Analysis of closure in fatigue crack growth. J. Appl. Mech. 45:1978;267-270.
    • (1978) J. Appl. Mech. , vol.45 , pp. 267-270
    • Budiansky, B.1    Hutchinson, J.W.2
  • 5
    • 0024703458 scopus 로고
    • On the cyclic J-integral applied to fatigue cracking
    • Chow C.L., Lu T.J. On the cyclic J-integral applied to fatigue cracking. Int. J. Fract. 40:1989;R53-R59.
    • (1989) Int. J. Fract. , vol.40
    • Chow, C.L.1    Lu, T.J.2
  • 6
    • 0014809315 scopus 로고
    • Fatigue crack closure under cyclic tension
    • Elber W. Fatigue crack closure under cyclic tension. Eng. Fract. Mech. 2:1970;37-45.
    • (1970) Eng. Fract. Mech. , vol.2 , pp. 37-45
    • Elber, W.1
  • 8
    • 0007082331 scopus 로고
    • Effects of thickness on fatigue crack initiation and growth in notched mild steel specimens
    • Jack A.R., Price A.T. Effects of thickness on fatigue crack initiation and growth in notched mild steel specimens. Acta Metall. 20:1972;857-866.
    • (1972) Acta Metall. , vol.20 , pp. 857-866
    • Jack, A.R.1    Price, A.T.2
  • 9
    • 84862782134 scopus 로고
    • Specimen size considerations in fatigue crack growth rate testing
    • James L.A. Specimen size considerations in fatigue crack growth rate testing. ASTM STP. 738:1981;45-57.
    • (1981) ASTM STP , vol.738 , pp. 45-57
    • James, L.A.1
  • 10
    • 0016070904 scopus 로고
    • Fatigue crack propagation and cyclic deformation at a crack tip
    • Kang T.S., Liu H.W. Fatigue crack propagation and cyclic deformation at a crack tip. Int. J. Fract. 10:1974;201-222.
    • (1974) Int. J. Fract. , vol.10 , pp. 201-222
    • Kang, T.S.1    Liu, H.W.2
  • 11
    • 0342462434 scopus 로고    scopus 로고
    • Effect of specimen thickness on the near-threshold fatigue crack propagation of nuclear structural materials
    • Taejon, Korea
    • E.S. Kim, I.S. Kim, 1998. Effect of specimen thickness on the near-threshold fatigue crack propagation of nuclear structural materials. In: Proc. of Workshop on the Integrity of Nuclear Power Plant Equipment, Taejon, Korea, pp. 143-158.
    • (1998) In: Proc. of Workshop on the Integrity of Nuclear Power Plant Equipment , pp. 143-158
    • Kim, E.S.1    Kim, I.S.2
  • 12
    • 0025904121 scopus 로고
    • The characterization of a crack-tip field
    • Liu H.W., Chen Q., Sinha S.K. The characterization of a crack-tip field. Eng. Frac. Mech. 39:1991;213-217.
    • (1991) Eng. Frac. Mech. , vol.39 , pp. 213-217
    • Liu, H.W.1    Chen, Q.2    Sinha, S.K.3
  • 13
    • 0025479405 scopus 로고
    • An examination of the reasons for the discrepancy between long and small fatigue cracks in Al-Li alloys
    • Nicholls D.J., Martin J.W. An examination of the reasons for the discrepancy between long and small fatigue cracks in Al-Li alloys. Mater. Sci. Eng. A128:1990;141-145.
    • (1990) Mater. Sci. Eng. , vol.128 , pp. 141-145
    • Nicholls, D.J.1    Martin, J.W.2
  • 15
    • 49349121254 scopus 로고
    • Continuing crack-tip deformation and fracture for plane-strain crack growth in elastic-plastic solids
    • Rice J.R., Sorensen E.P. Continuing crack-tip deformation and fracture for plane-strain crack growth in elastic-plastic solids. J. Mech. Phys. Solids. 26:1978;163-186.
    • (1978) J. Mech. Phys. Solids , vol.26 , pp. 163-186
    • Rice, J.R.1    Sorensen, E.P.2
  • 16
    • 0016993991 scopus 로고
    • Influence of section thickness on fatigue crack growth in Type 304 stainless steel
    • Shahinian P. Influence of section thickness on fatigue crack growth in Type 304 stainless steel. Nucl. Tech. 30:1976;390-397.
    • (1976) Nucl. Tech. , vol.30 , pp. 390-397
    • Shahinian, P.1
  • 18
    • 0027844785 scopus 로고
    • The plasticity aspect of fatigue crack growth
    • Wang G.S. The plasticity aspect of fatigue crack growth. Eng. Fract. Mech. 46:1993;909-930.
    • (1993) Eng. Fract. Mech. , vol.46 , pp. 909-930
    • Wang, G.S.1
  • 19
    • 0026377633 scopus 로고
    • A strip model for fatigue crack growth predictions under general load conditions
    • Wang G.S., Blom A.F. A strip model for fatigue crack growth predictions under general load conditions. Eng. Fract. Mech. 40:1991;507-533.
    • (1991) Eng. Fract. Mech. , vol.40 , pp. 507-533
    • Wang, G.S.1    Blom, A.F.2
  • 20
    • 0016034446 scopus 로고
    • Quasi-static extension of a tensile crack contained in a viscoelastic-plastic solid
    • Wnuk M.P. Quasi-static extension of a tensile crack contained in a viscoelastic-plastic solid. J. Appl. Mech. 41:1974;234-242.
    • (1974) J. Appl. Mech. , vol.41 , pp. 234-242
    • Wnuk, M.P.1
  • 21
    • 0020504472 scopus 로고
    • Extension of a stable crack at a variable growth step
    • Wnuk M.P., Mura T. Extension of a stable crack at a variable growth step. ASTM STP. 791:1983;96-127.
    • (1983) ASTM STP , vol.791 , pp. 96-127
    • Wnuk, M.P.1    Mura, T.2
  • 22
    • 0022593896 scopus 로고
    • Residual stress effects in fatigue crack growth
    • Woodtli J., Muster W., Radon J.C. Residual stress effects in fatigue crack growth. Eng. Fract. Mech. 24:1986;399-412.
    • (1986) Eng. Fract. Mech. , vol.24 , pp. 399-412
    • Woodtli, J.1    Muster, W.2    Radon, J.C.3


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.