Effect of heat treatment on the stress corrosion cracking behaviour of 403 stainless steel in NaCl at 95 °C

Materials Letters

Volumn 43, Issue 4, 2000, Pages 208-214

  Gonzalez Rodriguez, J G ^a   Bahena Martinez, G ^a   Salinas Bravo, V M ^b  

^a UNIVERSIDAD AUTÓNOMA DEL ESTADO DE MORELOS   (Mexico)

^b INSTITUTO DE INVESTIGACIONES ELÉCTRICAS   (Mexico)

Author keywords

[No Author keywords available]

Indexed keywords

ANNEALING; CRACK PROPAGATION; FAILURE ANALYSIS; FRACTURE MECHANICS; HYDROGEN EMBRITTLEMENT; MARTENSITIC TRANSFORMATIONS; MORPHOLOGY; QUENCHING; SODIUM CHLORIDE; STRAIN RATE; STRESS CORROSION CRACKING; TEMPERING;

INTERGRANULAR CRACKS; STAINLESS STEEL 403;

STAINLESS STEEL;

EID: 0033872974     PISSN: 0167577X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0167-577X(99)00261-X     Document Type: Article

References (14)

1. Lindinger R.J., Curvan R.M. Experience with stress corrosion cracking in large steam turbines. Corrosion 81. 1981;National Association of Corrosion Engineers, Toronto.
2. Viswanathan R., Riccardela P.C., Stein J. Stress corrosion cracking in turbine-generators. Life Prediction of Corrodable Structures. 1991;National Association of Corrosion Engineers, Kawai, HI.
3. Shalvoy R.S., Duglin S.K., Linderger R.J. The effect of turbine steam impurities on caustic stress corrosion cracking of NiCrMoV steels. Corrosion 81. 1981;National Association of Corrosion Engineers, Toronto.
4. Spachn H. Stress corrosion cracking and corrosion fatigue of martensitic, ferritic and ferritic-austenitic (duplex) stainless steels. Gangloff R.P., Ives M.B. Environment-Induced Cracking of Metals. 1988;449-487. NACE-10.
5. El-Sayed H.A., El-SubKi K.M., Kouda V.K. Surf. Technol. 16:1981;245.
6. Gouda V.K., El-Sayed H.A. Surf. Technol. 18:1983;327.
7. El-Sayed H.A., Gouda V.K. Corros. Prev. Control. 12:1986;142.
8. de Santa-Maria M.S., Thurnbull A. Corros. Sci. 29(1):1989;69.
9. Maier I.A., Galvele J.R. Corrosion. 36(2):1980;60.
10. Brown B.F. Stress corrosion cracking and hydrogen embrittlement of iron base alloys. Stahele R.W., Hochman J., McCright R.D., Slater J.E. National Association of Corrosion Engineers. 1973;. No. 5.
11. Knutsen R.D., Ball A. Corrosion. 47(5):1991;359.
12. Pourbaix M. Atlas of Electrochemical Equilibria. 1966;Pergamon, London.
13. Wilde B.E. Corrosion. 27(8):1971;326.
14. Doig P., Chastell D.J., Flewitt P.E.J. Met. Trans. 13A:1982;913.