The effect of aging on hydrogen trapping in precipitation-hardened alloys

Author keywords

Alloy; Hydrogen absorption; Potentiostatic; Steel

Indexed keywords

ABSORPTION; AGING; ALLOY; CORROSION RESISTANCE; HYDROGEN; HYDROGEN EMBRITTLEMENT; STEEL;

EID: 0033781211     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0010-938X(00)00036-6     Document Type: Article
Times cited : (25)

References (53)
  • 5
    • 0348097642 scopus 로고
    • Sc.D. Thesis, Massachusetts Institute of Technology, Cambridge, MA
    • J.W. Prybylowski, Sc.D. Thesis, Massachusetts Institute of Technology, Cambridge, MA, 1986.
    • (1986)
    • Prybylowski, J.W.1
  • 16
    • 85037517018 scopus 로고    scopus 로고
    • Pyromet® Alloy X-750 Carpenter Technology Corporation, Reading, PA
    • Alloy Data, Pyromet® Alloy X-750 Carpenter Technology Corporation, Reading, PA.
    • Alloy Data
  • 18
    • 0346836955 scopus 로고
    • Sc.D. Thesis, Massachusetts Institute of Technology, Cambridge, MA
    • C. Elliott, Sc.D. Thesis, Massachusetts Institute of Technology, Cambridge, MA, 1985.
    • (1985)
    • Elliott, C.1
  • 28
    • 0019684489 scopus 로고
    • I.M. Bernstein, A.W. Thompson (Eds.), TMS, Warrendale, PA
    • G.J. Thomas, in: I.M. Bernstein, A.W. Thompson (Eds.), Hydrogen Effects in Metals, TMS, Warrendale, PA, 1981, p. 77.
    • (1981) Hydrogen Effects in Metals , pp. 77
    • Thomas, G.J.1
  • 39
    • 0023669964 scopus 로고
    • R.A. Oriani, J.P. Hirth, M. Smialowski (Eds.), Noyes Publications, Park Ridge, NJ
    • I.M. Bernstein, G.M. Pressouyre, in: R.A. Oriani, J.P. Hirth, M. Smialowski (Eds.), Hydrogen Degradation of Ferrous Alloys, Noyes Publications, Park Ridge, NJ, 1985, p. 641.
    • (1985) Hydrogen Degradation of Ferrous Alloys , pp. 641
    • Bernstein, I.M.1    Pressouyre, G.M.2
  • 44
    • 0346836951 scopus 로고
    • AFML-72-102
    • M.T. Wang, Technical Report, AFML-72-102, Part I, 1972; Ref. 105 in "The stress corrosion and hydrogen embrittlement behavior of maraging steels", Proc. Conf. on Stress Corrosion Cracking and Hydrogen Embrittlement of Iron-Base Alloys, NACE, Houston, TX, 1973, p. 798.
    • (1972) Technical Report , Issue.1 PART
    • Wang, M.T.1
  • 45
    • 0003585113 scopus 로고
    • The stress corrosion and hydrogen embrittlement behavior of maraging steels
    • Ref. 105 in NACE, Houston, TX
    • M.T. Wang, Technical Report, AFML-72-102, Part I, 1972; Ref. 105 in "The stress corrosion and hydrogen embrittlement behavior of maraging steels", Proc. Conf. on Stress Corrosion Cracking and Hydrogen Embrittlement of Iron-Base Alloys, NACE, Houston, TX, 1973, p. 798.
    • (1973) Proc. Conf. on Stress Corrosion Cracking and Hydrogen Embrittlement of Iron-Base Alloys , pp. 798


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.