Crack tip morphology of slowly growing cracks in glass

Journal of the American Ceramic Society

Volumn 83, Issue 2, 2000, Pages 415-417

  Hénaux, Stéphane ^a,b   Creuzet, François ^a  

^a CNRS   (France)

^b CEA LETI   (France)

Author keywords

[No Author keywords available]

Indexed keywords

ATOMIC FORCE MICROSCOPY; CRACKS; DEFORMATION; MORPHOLOGY; VICKERS HARDNESS TESTING;

SODA LIME SILICA GLASS; SURFACE DEFORMATION;

GLASS;

EID: 0033733237     PISSN: 00027820     EISSN: None     Source Type: Journal    
DOI: 10.1111/j.1151-2916.2000.tb01207.x     Document Type: Article

References (14)

1. G. I. Barenblatt, "The Mathematical Theory of Equilibrium Cracks in Brittle Fracture," Adv. Appl. Mech., 7, 55-129 (1962).
2. D. S. Dugdale, "Yielding of Steel Sheels Containing Slits," J. Mech. Phys. Solids, 8, 100-104 (1960).
3. W. B. Hillig, "A General Inquiry into Fracture Toughness": pp. 21-35 in NATO Conference Series, 6, Vol. 11, Strength of Inorganic Glass. Edited by C. R. Kurkjian. Plenum Press, New York, 1985.
4. 2 Glass by High-Resolution Electron Microscopy," J. Am. Ceram. Soc., 67 [3] C-36-C-37 (1984).
5. B. R. Lawn, B. J. Hockey, and S. M. Wiederhorn, "Atomically Sharp Cracks in Brittle Solids: An Electron Microscopy Study," J. Mater. Sci., 15, 1207-23 (1980).
6. E. Guilloteau, H. Charrue, and F. Creuzet, "The Direct Observation of the Core Region of a Propagating Fracture Crack in Glass," Europhvs. Lett., 34 [7] 549-53 (1996).
7. J. C. Newman and I. S. Raju, "An Empirical Stress-Intensity Factor Equation for the Surface Crack," Eng. Fract. Mech., 15 [1-2] 185-92 (1981).
8. P. Dwivedi and D. Green, "Indentation Crack-Shape Evolution During Subcritical Crack Growth," J. Am. Ceram. Soc., 78 [5] 1240-46 (1995).
9. S. Hénaux and F. Creuzet, "Kinetic Fracture of Glass at the Nanometer Scale," J. Mater. Sci., Lett., 16, 1008-11 (1997).
10. B. R. Lawn, Fracture of Brittle Solids. Cambridge University Press, Cambridge, U.K., 1993.
11. P. S. Theocaris, "The Caustic as a Means to Define the Core Region in Brittle Fracture," Eng. Fract. Mech., 14, 353-62 (1981).
12. T. A. Michalske and S. W. Freiman, "A Molecular Interpretation of Stress Corrosion in Silica," Nature (London), 295, 511-12 (1982).
13. W. G. Knauss "Delayed Failure - The Griffith Problem for Linearity Viscoelastic Materials," Int. J. Fract. Mech., 6 [1] 7-20 (1970).
14. R. A. Schapery, "A Theory of Crack Initiation and Growth in Viscoelastic Media," Int. J. Fract., 11, 141-59, 369-88, 549-62 (1975).