Rate of strength decrease of fiber-reinforced ceramic-matrix composites during fatigue

Journal of the American Ceramic Society

Volumn 83, Issue 6, 2000, Pages 1469-1475

  Sørensen, Bent F ^a   Holmes, John W ^b   Vanswijgenhoven, Eddy L ^c  

^a TECHNICAL UNIVERSITY OF DENMARK   (Denmark)

^b UNIVERSITY OF MICHIGAN   (United States)

^c UNIVERSITY OF LEUVEN   (Belgium)

Author keywords

[No Author keywords available]

Indexed keywords

CALCIUM COMPOUNDS; CERAMIC FIBERS; FAILURE (MECHANICAL); FATIGUE OF MATERIALS; FIBER REINFORCED MATERIALS; MICROSTRUCTURE; SILICON CARBIDE; TENSILE PROPERTIES; ZEOLITES;

CALCIUM ALUMINUMSILICATE; RESIDUAL STRENGTH;

CERAMIC MATRIX COMPOSITES;

EID: 0033687409     PISSN: 00027820     EISSN: None     Source Type: Journal    
DOI: 10.1111/j.1151-2916.2000.tb01412.x     Document Type: Article

References (42)

1. J. W. Holmes and B. F. Sørensen, "Fatigue Behavior of Continuous-Fiber-Reinforced Ceramic Matrix Composites"; pp. 261-326 in Elevated Temperature Behavior of Ceramic Matrix Composites. Edited by S. V. Nair and K. Jakus. Butterworth Heineman, Newton, MA, 1995.
2. P. Karandikar and T.-W. Chou, "Damage Development and Moduli Reductions in Nicalon-Calcium Aluminosilicate Composites under Static Fatigue and Cyclic Fatigue," J. Am. Ceram. Soc., 76, 1720-28 (1993).
3. D. S. Beyerle, S. M. Spearing, F. W. Zok, and A. G. Evans, "Damage and Failure in Unidirectional Ceramic-Matrix Composites," J. Am. Ceram. Soc., 75, 2719-25 (1992).
4. B. F. Sørensen and R. Talreja, "Analysis of Damage in Ceramic Matrix Composites," Int. J. Damage Mech., 2, 246-71 (1993).
5. B. Budiansky, J. W. Hutchinson, and A. G. Evans, "Matrix Fracture in Fiber-Reinforced Ceramics," J. Mech. Phys. Solids, 34, 167-78 (1986).
6. L. N. McCartney, "Mechanics of Matrix Cracking in Brittle-Matrix Fiber-Reinforced Composites," Proc. R. Soc. London, A409, 329-50 (1987).
7. Y. J. Weitsman and H. Zhu, "Multi-fracture of Ceramic Composites," J. Mech. Phys. Solids, 41, 351-88 (1993).
8. W. A. Curtin, "Theory of Mechanical Properties of Ceramic Matrix Composites," J. Am. Ceram. Soc., 74, 2837-45 (1991).
9. J. W. Holmes and X. Wu, "Elevated Temperature Creep Behavior of Continuous Fiber-Reinforced Ceramics"; pp. 193-260 in Elevated Temperature Behavior of Ceramic Matrix Composites. Edited by S. V. Nair and K. Jakus. Butterworth Heineman, Newton, MA, 1995.
10. L. Filipuzzi, G. Camus, R. Naslain, and J. Thébault, "Oxidation Mechanisms and Kinetics of ID-SiC/C/SiC Composite Materials: I, An Experimental Approach," J. Am. Ceram. Soc., 70, 459-66 (1996).
11. A. G. Evans, F. W. Zok, R. M. McMeeking, and Z. Z. Du, "Models of High-Temperature, Environmentally Assisted Embrittlement in Ceramic Matrix Composites," J. Am. Ceram. Soc., 79, 2345-52 (1996).
12. R. F. Cooper and K. Chyung, "Structure and Chemistry of Fiber-Matrix Interfaces in Silicon Carbide Fiber-Reinforced Glass-Ceramic Composites: An Electron Microscopy Study," J. Mater. Sci., 22, 3148-69 (1987).
13. L. A. Bonney and R. F. Cooper, "Reaction Layer Interfaces in SiC-Fiber-Reinforced Glass-Ceramics: A High-Resolution Scanning Transmission Electron Microscopy Analysis," J. Am. Ceram. Soc., 73, 2916-26 (1990).
14. K. M. Prewo, "Fatigue and Stress Rupture of Silicon Carbide Fiber-Reinforced Glass-Ceramics," J. Mater. Sci., 22, 2695-701 (1987).
15. L. M. Butkus, L. P. Zawada, and G. A. Hartman, "Room Temperature Tensile and Fatigue Properties of Silicon Carbide Fiber-Reinforced Ceramic Matrix Composites"; in Aeromat'90, Advanced Aerospace Materials/Processes Conference (Long Beach, CA, May 21-24, 1990), 1990.
16. J. W. Holmes and S. F. Shuler, "Temperature Rise During Fatigue of Fiber-Reinforced Ceramics," J. Mater. Sci. Lett., 9, 1290-91 (1990).
17. J. W. Holmes and C. Cho, "Experimental Observations of Factional Heating in Fiber-Reinforced Ceramics," J. Am. Ceram. Soc., 75, 929-38 (1992).
18. L. P. Zawada, L. M. Butkus, and G. A. Hartman, "Room Temperature Tensile and Fatigue Properties of Silicon Carbide Fiber-Reinforced Aluminosilicate Glass," Ceram. Eng. Sci. Proc., 11, 1592-606 (1990).
19. D. Rouby and P. Reynaud, "Fatigue Behavior Related to the Interface Modification during Load Cycling in Ceramic-Matrix Composites," Compos. Sci. Technol., 48, 109-18 (1993).
20. J. W. Holmes, X. Wu, and B. F. Sørensen, "Frequency Dependency of Fatigue Life and Internal Heating of a Fiber-Reinforced Ceramic Matrix Composite," J. Am. Ceram. Soc., 77, 3284-86 (1994).
21. A. G. Evans, F. W. Zok, and R. M. McMeeking, "Fatigue of Ceramic Matrix Composites," Acta Metall. Mater., 43, 859-75 (1995).
22. C. Cho, J. W. Holmes, and J. R. Barber, "Estimation of Interfacial Shear in Ceramic Composites from Frictional Heating Measurements," J. Am. Ceram. Soc., 74, 2808-18 (1991).
23. E. Y. Luh and A. G. Evans, "High-Temperature Mechanical Properties of a Ceramic Matrix Composite," J. Am. Ceram. Soc., 70, 466-69 (1987).
24. K. M. Prewo, B. Johnson, and S. Starrett, "Silicon Carbide Fibre-Reinforced Glass-Ceramic Composite Tensile Behaviour at Elevated Temperature," J. Mater. Sci., 24, 1373-79 (1989).
25. 4-Matrix Composites," J. Am. Ceram. Soc., 75, 406-12 (1992).
26. J. F. Mandell, D. H. Grande, and J. Jacobs, "Tensile Behaviour of Glass/Ceramic Composite Materials at Elevated Temperatures," J. Eng. Gas Turbines Power, 109, 267-73 (1987).
27. J. W. Holmes, "Influence of Stress Ratio on the Elevated-Temperature Fatigue of Silicon Carbide Fiber-Reinforced Silicon Nitride Composite," J. Am. Ceram. Soc., 74, 1639-45 (1991).
28. J. W. Holmes, "A Technique for Tensile Fatigue and Creep Testing of Fiber-Reinforced Ceramics." J. Compos. Mater., 26, 915-32 (1992).
29. A. W. Pryce and P. A. Smith, "Matrix Cracking in Unidirectional Ceramic Matrix Composites under Quasi-Static and Cyclic Loading," Acta Metall. Mater., 41, 1269-81 (1993).
30. W. P. Keith and K. T. Kedward, "The Stress-Strain Behavior of a Porous Unidirectional Ceramic Matrix Composite," Composites, 26, 163-74 (1995).
31. B. F. Sørensen and J. W. Holmes, "Model of the Mechanical Behavior of Continuous Fiber Reinforced Ceramic Matrix Composites During Cyclic Loading," J. Eur. Ceram. Soc., submitted.
32. T. Mackin and F. W. Zok, "Fiber Bundle Pushout: A Technique for the Measurement of Interfacial Sliding Properties," J. Am. Ceram. Soc., 75, 3169-71 (1992).
33. E. Lara-Curzio and M. K. Feber, "Methodology for the Determination of the Interfacial Properties of Brittle Matrix Composites," J. Mater. Sci., 29, 6152-58 (1994).
34. B. F. Sørensen and J. W. Holmes, "Effect of Loading Rate on the Monotonie Tensile Behavior and Matrix Cracking of a Fiber-Reinforced Ceramic," J. Am. Ceram. Soc., 79, 313-20 (1996).
35. R. W. Goettler and K. T. Faber, "Interfacial Shear Stress in Fiber-Reinforced Glasses," Compos. Sci. Technol., 37, 129-47 (1989).
36. B. F. Sørensen and J. W. Holmes, "Fatigue of Continuous Fiber-Reinforced Ceramic Matrix Composites: Review of Mechanisms and Models"; pp. 487-500 in Proceedings of the International Symposium on Fatigue under Thermal and Mechanical Loading. Edited by J. Bressers and L. Remy. Kluwer Academic Publishers, Dordrecht, Netherlands, 1996.
37. S. M. Spearing, F. M. Zok, and A. G. Evans, "Stress Corrosion Cracking in a Unidirectional Ceramic-Matrix Composite," J. Am. Ceram. Soc., 77, 562-70 (1994).
38. B. F. Sørensen and J. W. Holmes, "Influence of Stress Ratio on the Fatigue Life of a Continuous Fiber-Reinforced Ceramic Matrix Composite," unpublished work.
39. J. W. Holmes, unpublished research.
40. 4 Composite," Scr. Metall. Mater., 32, 1085-89 (1995).
41. J. I. Eldridge, R. T. Bhatt, and N. P. Bansal, "Investigation of Fiber/Matrix Interfacial Mechanical Behavior in Ceramic Matrix Composites by Cyclic Fiber Push-in Testing," Ceram. Eng. Sci. Proc., 17, 266-78 (1996).
42. W. A. Thomas and J. M. Sanchez, "Influence of Interfacial Sliding Stress on Fatigue Behavior of Oxidized Nicalon/Calcium Aluminosilicate Composites," J. Am. Ceram. Soc., 79, 2659-65 (1996).