Practical usefulness of a `marker-technique' to the examination of crack growth behaviour of Ni-alloys at 500 to 750 °C;Risswachstum markieren - Untersuchungen an Nickel-Legierungen bei 500 und 750 °C

Materialpruefung/Materials Testing

Volumn 42, Issue 9, 2000, Pages 340-348

  Schwarze, Dietmar ^a   Klabbers, ^a   Schubert, Florian ^a  

^a NONE

Author keywords

[No Author keywords available]

Indexed keywords

CRACK INITIATION; CREEP; FATIGUE OF MATERIALS; HARDENING; NICKEL ALLOYS; STRUCTURAL LOADS; CRACKS; FATIGUE CRACK PROPAGATION; GROWTH RATE; TURBINE COMPONENTS;

INCONEL 617; MARKER-TECHNIQUE;

CRACK PROPAGATION; NICKEL ALLOYS;

CRACK GROWTH EVALUATIONS; CREEP CRACK GROWTH; CRITICAL CONDITION; INDUSTRIAL GAS TURBINES; LOADING CONDITION; NICKEL BASE ALLOYS; SERVICE TEMPERATURE; TEMPERATURE RANGE;

EID: 0033633170     PISSN: 00255300     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (5)

1. Lecomte-Beckers, J., Schubert, F., Ennis, P.J.: Materials for Advanced Power Engineering 1998. Proc. of the 6th Liège Conference 1998
2. Schubert, F.: "Entwicklung eines strukturabhängigen Werkstoffmodells für komplexe Hochtemperaturberechnungen, Beispiel, Turbinenscheibe", Vortrag BMBF-Verbundprojekt 03 M 3007 (1992)
3. Schwarze, D.: Anwendbarkeit einer "Marker-Technik" zur Unterstützung von Risswachstumsuntersuchungen in spröden und duktilen Ni-Legierungen bei 500 und 750° C. Dissertation RWTH Aachen 1999
4. Weber, M.: Risswachstum in der PM-Nickelbasis- Legierung PM N18 bei Temperaturen zwischen 400 und 750° C unter statischer und zyklischer Belastung. Dissertation RWTH Aachen 1994
5. Penkalla, H. J., Schubert, F., Nickel, H: Alloy 617 tubes at high temperatures. Conf. Proc. of Superalloys, Seven Springs 1988, Met. Soc., 1988, p. 2-12