Hydrogen effects in the corrosion fatigue behaviour of the white zone of 7xxx series aluminium alloy welds

Corrosion Science

Volumn 42, Issue 1, 2000, Pages 17-33

  Kotsikos, G ^a   Sutcliffe, J M ^b   Holroyd, N J H ^c  

^a NEWCASTLE UNIVERSITY   (United Kingdom)

^b UNIVERSITY OF ABERTAY DUNDEE   (United Kingdom)

^c Luxfer Gas Cylinders Inc   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ALUMINUM ALLOY; FATIGUE; HYDROGEN; WELD;

ALUMINUM ALLOYS; CORROSION FATIGUE; CRACK INITIATION; CRACK PROPAGATION; CYCLIC LOADS; HYDROGEN EMBRITTLEMENT; WELDS;

ALUMINUM ALLOY 7017-T651;

ALUMINUM CORROSION;

EID: 0033622719     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0010-938X(99)00047-5     Document Type: Article

References (26)

1. Reboul M.C., Dubost B., Lashermes M. Corrosion Science. 11:(25):1985;999-1018.
2. S.S. Birley, Proceedings of Environmental Degradation of Engineering Materials III, Penn State University, PA, USA, 1987, p. 281.
3. Kent K.G. Metall. Rev. 15:1970;135-140.
4. Kotsikos G., Sutcliffe J.M., Holroyd N.J.H. British Corrosion Journal. 30:(4):1995;302-308.
5. Ewalds H.L., Wanhill R.J.H. Fracture Mechanics. 1984;Arnold, London.
6. Kruger S., Bird C.E. Br. Corros. J. 13:1978;163-166.
7. Speidel M.O. Fundamental Aspects of Stress Corrosion Cracking. 1969;561-576 NACE, Houston, TX.
8. J.M. Austen, E.F. Walker, International conference on the effects of environment in fatigue, Publication 1977-4, London, The Institution of Mechanical Engineers (1977) 1-10.
9. Scamans G.M. Metall. Trans., A. 11A:1980;846-850.
10. R.J. Gest, A.R. Troiano, in: Proceedings of the Conference on Hydrogen Effects in Metals, Paris, 1972, p. 427.
11. Scamans G.M., Alani R., Swan P.R. Coros. Sci. 16:1976;443.
12. Koch G.H. Corrosion. 35:1979;73.
13. Holroyd N.J.H., Hardie D. Factors controlling crack velocity in 7xxx series aluminium alloys during fatigue in an aggressive environment. Corr. Sci. 23:(6):1983;527-546.
14. Parkins R.N., Greenwell B.S. The interface between cf and scc. Metal. Sci. 11:1977;405-411.
15. Parkins R.N., Suzuki Y. Conference on Low Cyclic Loading Effects in Environment Sensitive Fracture, Milan. 1982.
16. Holroyd N.J.H., Hardie D. Strain rate effects on environmentally assisted fracture of a commercial high strength aluminium alloy. Corros. Sci. 21:(2):1981;129.
17. Holroyd N.J.H., Hardie D. Corros. Sci. 21:1981;129-144.
18. Christodoulou L., Flower H.M. Acta Metall. 28:1980;481-487.
19. Tien J.K., Richards R.J., Buck O., Markus H.L. Scripta Met. 9:1975;1097.
20. Tien J.K., Nair S.V., Bates R.C., Buck O. Scripta Met. 14:1980;591.
21. Ratke L., Gruhl W. Werkst. U. Korros. 31:1980;768.
22. Hermann R., Birley S.S., Holdway P. Materials Science & Engineering. A212:1996;247-255.
23. Schmiedel H., Gruhl W. Contribution on the scc behaviour of weld joints in Al-Zn-Mg alloys. Metall. 38:1984;1.
24. G.M. Scamans, C.D.S. Tuck, in: International conference on mechanisms of environment sensitive cracking of materials, University of Surrey, 1977, p. 482.
25. Scamans G.M., Holroyd N.J.H., Tuck C.D.S. Role of Mg segregation in the intergranular stress corrosion cracking of Aluminium alloys. Corr. Sci. 27:(4):1987;329-347.
26. Gest R.J., Troiano A.R. Corrosion. 30:1974;274.