Edge-cracks in single crystals under monotonic and cyclic loads

International Journal of Fracture

Volumn 99, Issue 1-2, 1999, Pages 81-95

  Hutchinson, John W ^a   Tvergaard, Viggo ^b  

^a HARVARD UNIVERSITY   (United States)

^b TECHNICAL UNIVERSITY OF DENMARK   (Denmark)

Author keywords

Edge cracks; Fatigue; Large scale yielding; Single crystal

Indexed keywords

CRACK PROPAGATION; CYCLIC LOADS; FATIGUE OF MATERIALS; PLASTICITY; SHEAR STRESS; SINGLE CRYSTALS; STRAIN;

CRACK ORIENTATION; CRACK OVERCOMING BARRIERS; CRACK TIP OPENING; EDGE CRACKS; LARGE SCALE YIELDING; MONOTONIC LOADS; PRIMARY SLIP PLANE; SLIDING DISPLACEMENTS;

CRACKS;

CRACK PROPAGATION; FATIGUE;

EID: 0033503957     PISSN: 03769429     EISSN: None     Source Type: Journal    
DOI: 10.1023/a:1018323725736     Document Type: Article

References (13)

1. Barenblatt, G.I. (1959a). The formulation of equilibrium cracks during brittle fracture. General ideas and hypotheses. Axially-symmetric cracks. Journal of Applied Mathematics and Mechanics 23, 622-636. (Translation from Russian: PMM 23 (1959a), 434-444).
2. Barenblatt, G.I. (1959a). The formulation of equilibrium cracks during brittle fracture. General ideas and hypotheses. Axially-symmetric cracks. Journal of Applied Mathematics and Mechanics 23, 622-636. (Translation from Russian: PMM 23 (1959a), 434-444).
3. Barenblatt, G.I. (1959b). The formulation of equilibrium cracks during brittle fracture. Rectilinear cracks in plane plates. Journal of Applied Mathematics and Mechanics 23, 1009-1029. (Translation from Russian: PMM 23 (1959b), 706-721).
4. Barenblatt, G.I. (1959b). The formulation of equilibrium cracks during brittle fracture. Rectilinear cracks in plane plates. Journal of Applied Mathematics and Mechanics 23, 1009-1029. (Translation from Russian: PMM 23 (1959b), 706-721).
5. Barenblatt, G.I. (1962). The mathematical theory of equilibrium cracks in brittle fracture. Advances in Applied Mechanics 7, 55-129.
6. Dugdale, D.S. (1960). Yielding of steel sheets containing slits. Journal of the Mechanics and Physics of Solids 8, 100-108.
7. Isida, M. (1979). Tension of a half plane containing array cracks, branched cracks and cracks emanating from sharp notches. Transaction of the Japan Society for Mechanical Engineers 45, 306-317.
8. Ma, B.-T. and Laird, C. (1989). Overview of fatigue behavior in copper single crystals: I, II & III. Acta Metallurgica 37, 325-336, 337-348, 349-355.
9. McDowell, D.L. (1996). Basic issues in the mechanics of high cycle metal fatigue. International Journal of Fracture 80, 103-145.
10. Miller, K.J. (1993). Materials science perspective of metal fatigue resistance. Materials Science and Technology 9, 453-462.
11. Repetto, E.A. and Ortiz, M. (1977). A micromechanical model of fatigue crack nucleation in FCC metals. Acta Materialia 45, 2577-2595.
12. Rice, J.R. (1967). Mechanics of Crack Tip Deformation and Extension by Fatigue. ASTM STP 415, American Society of Testing Materials, 247-309.
13. Saeedvafa, M. and Rice, J.R. (1992). Crack tip fileds in a material with three independent slip systems: NiAl single crystal. Modelling and Simulation in Materials Science and Engineering 1, 53-71.